It was aimed to improve the surface properties of the steel materials which coating by aluminium were applied. In this study, on surface in materials Ç 1020 and AISI 316 was applied Al coating by hot dip method. This process was applied to aluminium at temperature of 750 °C, for 2 and 10 minutes. Samples of Al coated were subjected to diffusion treatment at 800 °C for 1 and 6 hours in notr media. With applied heat treatment processes after coating process were examined on surface microstructure and the changes in the thickness of diffusion layer or Al layer by microhardness values.
Özet
Çelik malzemelerin yüzey özelliklerini iyileştirmek amacıyla, yüzeyleri alüminyum ile kaplama yapılmaktadır. Bu çalışmada, az karbonlu çelik (Ç1020) ve paslanmaz çelik (AlSI 316)malzemelerin yüzeyine sıcak daldırma yöntemiyle Al kaplama yapılmıştır. Bu işlem 750 °C sıcaklıkta, 2 ve 10 dak süreyle bekletilerek uygulanmıştır. Al kaplama uygulanan numunelere, nötr ortamda 800 °C sıcaklıkta ve 1 ve 6 saat süreyle difüzyon tavlaması uygulanmıştır. Kaplama işlemi sonrası uygulanan ısıl işlemlerle yüzey mikroyapısı ve mikrosertlik ölçümler yardımıyla Al ve difüzyon tabakalarındaki kalınlık değişimi incelenmiştir.