It was also proven that for feedstock comprised of 69wt% Ti-6Al-7Nb powder, the suitable set of sintering parameters were as follows: sintering temperature of 1250 °C, dwell time of 60 min, heating rate of 1 °C/min, gas flow rate of 5 L/min.
📌 3 Maddede Bu Makale
🎯
Amaç & Hipotez:In this study, the optimized sintering parameters for a feedstock obtained by mixing the powder of Ti-6Al-7Nb and 31wt% binder system (comprised of high-density polyethylene, Polypropylene, PEG 20000, paraffin wax and stearic acid), were determined.
📊
Temel Bulgular & Veri:In order to produce a component, Taguchi method was applied to obtain the optimum conditions.
💡
Sonuç & Katkı:It was also proven that for feedstock comprised of 69wt% Ti-6Al-7Nb powder, the suitable set of sintering parameters were as follows: sintering temperature of 1250 °C, dwell time of 60 min, heating rate of 1 °C/min, gas flow rate of 5 L/min.
In this study, the optimized sintering parameters for a feedstock obtained by mixing the powder of Ti-6Al-7Nb and 31wt% binder system (comprised of high-density polyethylene, Polypropylene, PEG 20000, paraffin wax and stearic acid), were determined. In order to produce a component, Taguchi method was applied to obtain the optimum conditions. As a result of ANOVA, sintering temperature was proven to be the most effective one. It was also proven that for feedstock comprised of 69wt% Ti-6Al-7Nb powder, the suitable set of sintering parameters were as follows: sintering temperature of 1250 °C, dwell time of 60 min, heating rate of 1 °C/min, gas flow rate of 5 L/min.
SUBAŞI, M. (2017). An Investigation of Sintering Parameters of Ti-6Al-7Nb Fabricated by Powder Injection Molding. Gazi University Journal of Science, Cilt: 30 - Sayı: 4, 502–512. https://ajindex.com/articles/254896
Lee, W.-S. and Chen, C.-W., "Dynamic mechanical properties and microstructure of Ti–6Al–7Nb biomedical alloy as function of strain rate", Materials Science and Technology, 29(9), 1055-1064, (2013).