KaydedilenlerDerginizi ekleyin

Dergiler / Gazi University Journal of Science / 2023 / Cilt: 36 Sayı: 4

Investigation of Sinterability of WC-Co Component Comprising of AISI 4340 Steel Inserts

Mehmet SUBAŞI
Harun KOÇAK
Asghar SAFARİAN
Çetin KARATAŞ
Sayfa
1722–1731
Yayın Tarihi
2023-12-01
DOI
—
🏛️Bu makalenin bibliyografik verileri ve tam metin bağlantısı DergiPark üzerinden sağlanmıştır.
DergiPark Kaydı ↗
✨

Yapay Zeka Hızlı Bakış & Çıkarımlar

AI Insight
⚡ TL;DR(1 Cümlede Hızlı Çıkarım)

As a result, the optimum sintering temperature and dwell time were determined to be 1300 °C and 240 min, respectively, at which the highest hardness, compression strength, and sintered density were obtained without any defects such as cracks or gaps.

📌 3 Maddede Bu Makale

🎯
Amaç & Hipotez:In this study, sinterability of WC-9% Co component with AISI 4340 steel insert was investigated using Inserted Powder Injection Molding (IPIM) method.
📊
Temel Bulgular & Veri:Sintering experiments were performed at temperatures of 1200 °C to 1350 °C with dwell times of 120, 240, 360 min.
💡
Sonuç & Katkı:As a result, the optimum sintering temperature and dwell time were determined to be 1300 °C and 240 min, respectively, at which the highest hardness, compression strength, and sintered density were obtained without any defects such as cracks or gaps.
🔬Tür:Araştırma Makalesi
📍Kapsam:Genişletilmiş Akademik Örneklem
⚙️Değişkenler:Inserted powder injection molding · WC-Co feedstock · AISI 4340 steel

Abstract

In this study, sinterability of WC-9% Co component with AISI 4340 steel insert was investigated using Inserted Powder Injection Molding (IPIM) method. Sintering experiments were performed at temperatures of 1200 °C to 1350 °C with dwell times of 120, 240, 360 min. Defects such as gaps, cracks and macro-porosities were observed in specimens, sintered at temperatures of 1200 °C and 1250 °C for all dwell times. It was proved that sintering temperature of 1350 °C was as high as it caused insert to get deformed and melted. As a result, the optimum sintering temperature and dwell time were determined to be 1300 °C and 240 min, respectively, at which the highest hardness, compression strength, and sintered density were obtained without any defects such as cracks or gaps.

🔖

Bu Makaleye Atıf Yap

SUBAŞI, M., KOÇAK, H., SAFARİAN, A., KARATAŞ, Ç. (2023). Investigation of Sinterability of WC-Co Component Comprising of AISI 4340 Steel Inserts. Gazi University Journal of Science, Cilt: 36 Sayı: 4, 1722–1731. https://ajindex.com/articles/1020140

📄 Tam Metin PDF Okuyucu

📄

PDF görüntüleyici hazırlanıyor...

Kaynakça (12)

  1. Karataş, Ç., Sarıtaş, S., "Toz enjeksiyonla kalıplama: Bir ileri teknoloji imalat metodu", Journal of the Faculty of Engineering and Architecture of Gazi University, 13(2): 193-228, (1998)
  2. German, R.M., Powder Injection Molding, In ASM Handbook: Powder Metal Technologies and Applications, (1998)
  3. Safarian, A., Subaşi, M. and Karataş, Ç., "Reducing debinding time in thick components fabricated by powder injection molding", International Journal of Materials Research, 106(5): 527-531, (2015)
  4. Safarian, A., Subaşi, M. and Karataş, Ç., "The effect of sintering parameters on diffusion bonding of 316L stainless steel in inserted metal injection molding", The International Journal of Advanced Manufacturing Technology, 89(5): 2165-2173, (2017)
  5. Koçak, H., Samet, K., Yılmaz, O. and Karataş, Ç., "Investigation of composite part production from WC-Co/HSS using nickel interlayer by inserted powder injection molding method", Gazi University Journal of Science Part C: Design and Technology, 6(2): 374-384, (2018)
  6. Johnson, J.L., Tan, L.K., Suri, P. and German, R.M., "Design guidelines for processing bi-material components via powder-injection molding", The Journal of The Minerals, Metals & Materials Society, 55(10): 30-34, (2003)
  7. Heaney, D.F., Suri, P. and German, R.M., "Defect-free sintering of two material powder injection molded components Part I Experimental investigations", Journal of Materials Science, 38(24): 4869-4874, (2003)
  8. Guo, Y., Wang, Y., Gao, B., Shi, Z. and Yuan, Z., "Rapid diffusion bonding of WC-Co cemented carbide to 40Cr steel with Ni interlayer: Effect of surface roughness and interlayer thickness", Ceramics International, 42(15): 16729-16737, (2016)
  9. Rodelas, J., Hilmas, G. and Mishra, R.S., "Sinterbonding cobalt-cemented tungsten carbide to tungsten heavy alloys", International Journal of Refractory Metals and Hard Materials, 27(5): 835-841, (2009)
  10. Simchi, A., Petzoldt, F., "Cosintering of powder injection molding parts made from ultrafine WC-Co and 316L stainless steel powders for fabrication of novel composite structures", Metallurgical and Materials Transactions A, 41(1): 233, (2009)
  11. Sun, Y., Su, W., Yang, H. and Ruan, J., "Effects of WC particle size on sintering behavior and mechanical properties of coarse grained WC–8Co cemented carbides fabricated by unmilled composite powders", Ceramics International, 41 (10): Part B, 14482-14491, (2015)
  12. Pötschke, J., Säuberlich, T., Vornberger, A. a