In this study, the effect of TiN coating by physical vapour deposition method on wear behaviour of austemperedductile iron was studied. For this purpose, austenitising at 900°C for 60 min and later austempering at 360 °C for30 and 90 min was applied to the specimens. After heat treatment, the surfaces of these samples were coated TiNby PVD method. Wear tests were performed on pin-on-disc device under loads of 20 N, 40 N and 60 N, at linearsliding speed of 1m/sec and sliding distance of 1800 m. The experimental results show that pearliticmicrostructure of ductile iron turned into ausferritic structure depending on heat treatment conditions. The wearof specimen was reduced 3-4 times by the effect of TiN coating.
Özet
Bu çalışmada, östemperlenmiş küresel grafitli dökme demirlerin aşınma davranışı üzerinde fiziksel buhar birikimmetodu ile TiN kaplamanın etkisi araştırılmıştır. Bu amaçla, 900°C‘de 60 dakika östenitleme, daha sonra 360°C’de 30 ve 90 dakika östemperleme işlemi uygulanmıştır. Isıl işlemden sonra numunelere PVD yöntemi ile TiNkaplanmıştır. Aşınma testleri, disk üzerinde pim cihazında 20 N, 40 N ve 60 N yükler altında, 1m/s kaymahızında 1800 m kayma mesafesinde gerçekleştirilmiştir. Deneysel sonuçlar, ısıl işlem şartlarına bağlı olarakküresel grafitli dökme demirin perlitik yapısının ösferrite dönüştüğünü göstermiştir. Numunelerin aşınması, TiNkaplamanın etkisi ile 3-4 kat azalmıştır.