AI InsightAccording to the experimental results; the highest retention rate was found in oak wood at a concentration of 3% (8.09%), the lowest retention rate in spruce wood at a concentration of 1% (1.18%), the highest air-dry specific gravity value was in oak wood at a concentration of 3% (0.64 g/cm³), the highest bending strength value was in oak wood at 3% (108.14 N/mm²), the highest compressive strength value was in oak wood at 1% (56 N/mm²), and the highest dynamic bending strength was in oak wood at 3% (0.82 kgm/cm²).
📌 3 Key Takeaways
Abstract
In this century, climate change, fires, earthquakes, depletion of water resources, and the rapidly increasing world population have further increased the importance of forest resources. Wood, being natural and environmentally friendly, has gained importance in this century and in the future due to its preservation with natural materials and even the reuse of used wood. An extract of the ecological material seaweed (Chlorophyta) was obtained and, at concentrations of 1% and 3% (distilled water/solvent), spruce (Picea orientalis (L)Link) and sessile oak (Quercus petraea Liebl.) wood were impregnated using vacuum methods according to ASTM D 1413-76 standards, and some of its technological properties were investigated. According to the experimental results; the highest retention rate was found in oak wood at a concentration of 3% (8.09%), the lowest retention rate in spruce wood at a concentration of 1% (1.18%), the highest air-dry specific gravity value was in oak wood at a concentration of 3% (0.64 g/cm³), the highest bending strength value was in oak wood at 3% (108.14 N/mm²), the highest compressive strength value was in oak wood at 1% (56 N/mm²), and the highest dynamic bending strength was in oak wood at 3% (0.82 kgm/cm²).
Özet
İçinde bulunduğumuz yüzyılda iklim değişiklikleri, yangınlar, depremler, su kaynaklarının azalması, hızla artan dünya nüfusu orman kaynağının önemini dahada artırmıştır. Ahşap doğal olması ve insan/çevre sağlığı yönüyle de dost yapısı ahşabın yine doğal gereçlerle korunması ve hatta kullanılan ahşabın tekrar kullanımı içinde bulunduğumuz yüzyılda ve gelecek süreçlerde önem kazanmıştır. Ekolojik materyal olan deniz yosununun (Chlorophyta) ekstraktı elde edilmiş ve %1, %3 oranlarında konsantrasyonları hazırlanarak (destile su/çözündürücü) ASTM D 1413-76 standardına göre vakumla ladin (Picea orientalis (L)Link) ve sapsız meşe (Quercus) odunlarının emprenyesi yapılarak bazı teknolojik özellikleri araştırılmıştır. Deney sonuçlarına göre; en yüksek tutunma miktarı(retensiyon) meşe odununda %3 konsantrasyon (%8.09), en düşük tutunma miktarı ladin odununda %1 konsantrasyonda (%1.18), en yüksek hava kurusu özgül ağırlık değeri meşe odununda %3 konsantrasyon (0.64 g/cm3), en yüksek eğilme direnci değeri %3 meşe odununda (108.14 N/mm2), en yüksek basınç direnci değeri %1 meşe odununda (56 N/mm2), en yüksek dinamik eğilme direnci %3 meşe odununda (0.82 kgm/cm2) belirlenmiştir.