One-step synthesis of hierarchical [B]-ZSM-5 using cetyltrimethylammonium bromide as mesoporogen

Büşra KARAKAYA YALÇIN
Bahar İPEK
Sayfa
841–858
Yayın Tarihi
2022-11-01
DOI
—
🏛️Bu makalenin bibliyografik verileri ve tam metin bağlantısı DergiPark üzerinden sağlanmıştır.
DergiPark Kaydı ↗
✨

Yapay Zeka Hızlı Bakış & Çıkarımlar

AI Insight
⚡ TL;DR(1 Cümlede Hızlı Çıkarım)

The textural properties, i.e. the surface areas and pore volumes are investigated using $N_2$ adsorption at–196 °C. t-plot micropore volume of 0.11 $cm^3$/g and mesopore volume of 0.14 $cm^3$/g are obtained applying this synthesismethod for mesopores having pore diameters within the range of 2–10 nm.

📌 3 Maddede Bu Makale

🎯
Amaç & Hipotez:One-step facile synthesis of boron containing ZSM-5 microspheres is developed using 1,6-diaminohexane asthe structure-directing agent and cetyltrimethylammonium bromide as the mesoporogen.
📊
Temel Bulgular & Veri:High boron incorporation upto Si/B ratio of 38 is achieved and evidenced by the stretching vibrations of B–O–Si at 667 $cm^{-1}$and 917 $cm^{-1}$ usingFourier-transform infrared spectra.
💡
Sonuç & Katkı:The textural properties, i.e. the surface areas and pore volumes are investigated using $N_2$ adsorption at–196 °C. t-plot micropore volume of 0.11 $cm^3$/g and mesopore volume of 0.14 $cm^3$/g are obtained applying this synthesismethod for mesopores having pore diameters within the range of 2–10 nm.
🔬Tür:Araştırma Makalesi
📍Kapsam:Genişletilmiş Akademik Örneklem
⚙️Değişkenler:Alan Parametreleri

Abstract

One-step facile synthesis of boron containing ZSM-5 microspheres is developed using 1,6-diaminohexane asthe structure-directing agent and cetyltrimethylammonium bromide as the mesoporogen. High boron incorporation upto Si/B ratio of 38 is achieved and evidenced by the stretching vibrations of B–O–Si at 667 $cm^{-1}$and 917 $cm^{-1}$ usingFourier-transform infrared spectra. The morphology of the crystals resembles berry-like spheres with sizes approximately15 µm, which is composed of aggregated nanocrystals having sizes around 450 nm, is observed using scanning electronmicroscopy. The textural properties, i.e. the surface areas and pore volumes are investigated using $N_2$ adsorption at–196 °C. t-plot micropore volume of 0.11 $cm^3$/g and mesopore volume of 0.14 $cm^3$/g are obtained applying this synthesismethod for mesopores having pore diameters within the range of 2–10 nm.

🔖

Bu Makaleye Atıf Yap

YALÇIN, B. K., İPEK, B. (2022). One-step synthesis of hierarchical [B]-ZSM-5 using cetyltrimethylammonium bromide as mesoporogen. Turkish Journal of Chemistry, Cilt: 44 - Sayı: 3, 841–858. https://ajindex.com/articles/601846

📄 Tam Metin PDF Okuyucu

📄

PDF görüntüleyici hazırlanıyor...

Kaynakça (10)

  1. Corma A. From microporous to mesoporous molecular sieve materials and their use in catalysis. Chemical Reviews 1997
  2. 97 (6): 2373-2419. doi: 10.1021/CR960406N 2. Hartmann M, Machoke AG, Schwieger W. Catalytic test reactions for the evaluation of hierarchical zeolites. Chemical Society Reviews 2016
  3. 45 (12): 3313-3330. doi: 10.1039/c5cs00935a 3. Townsend RP, Coker EN. Ion exchange in zeolites. In: Bekkum H van, Flanigen EM, Jacobs PA, Jansen JC (editors). Studies in Surface Science and Catalysis. Elsevier, 2001, pp. 467-524. doi: 10.1016/s0167-2991(01)80253-6 4. Lobo RF. Intermolecular Forces in Zeolite Adsorption and Catalysis. In: Valtchev V, Mintova S, Tsapatsis M (editors). Ordered Porous Solids: Recent Advances and Prospects. Amsterdam: Elsevier, 2009, pp. 239-261. doi: 10.1016/B978-0-444-53189-6.00009-3 5. Garcia Vargas N, Stevenson S, Shantz DF. Simultaneous isomorphous incorporation of boron and germanium in MFI zeolites. Microporous and Mesoporous Materials 2013
  4. doi: 10.1016/j.micromeso.2012.11.015 6. Přech J, Vitvarová D, Lupínková L, Kubů M, Čejka J. Titanium impregnated borosilicate zeolites for epoxidation catalysis. Microporous and Mesoporous Materials 2015
  5. doi: 10.1016/j.micromeso.2015.03.015 7. Kawagoe H, Komura K, Kim JH, Seo G, Sugi Y. Preparation of [Fe]-SSZ-24 through the isomorphous substitution of [B]-SSZ-24 with iron, and its catalytic properties in the isopropylation of biphenyl. Journal of Molecular Catalysis A: Chemical 2011
  6. 350 (1-2): 1-8. doi: 10.1016/j.molcata.2011.08.027 8. Millini R, Perego G, Bellussi G. Synthesis and characterization of boron-containing molecular sieves. Topics in Catalysis 1999
  7. 9 (1/2): 13-34. doi: 10.1023/A:1019198119365 9. Hu Z, Zhang H, Wang L, Zhang H, Zhang Y et al. Highly stable boron-modified hierarchical nanocrystalline ZSM5 zeolite for the methanol to propylene reaction. Catalysis Science and Technology 2014
  8. 4 (9): 2891-2895. doi: 10.1039/c4cy00376d 10. Millini R, Carluccio LC, Carati A, Parker WO. Synthesis and characterization of borosilicates with the EUO framework topology. Microporous and Mesoporous Materials 2001
  9. 46 (2-3): 191-201. doi: 10.1016/S1387-1811(01)00284- 0 11. Regli L, Bordiga S, Lamberti C, Lillerud KP, Zones SI et al. Effect of boron substitution in chabazite framework: IR studies on the acidity properties and reactivity towards methanol. Journal of Physical Chemistry C 2007
  10. 111 (7): 2992-2999. doi: 10.1021/jp064048w 12. Tong HTT, Koller H. Con