Effect of Ultrasonic Treatment Parameters on Microstructural and Mechanical Properties of A356 Aluminum Alloy

Esra DOKUMACI
Kazım ÖNEL
Uğur AYBARÇ
Sayfa
234–243
Yayın Tarihi
2022-10-19
DOI
—
🏛️Bu makalenin bibliyografik verileri ve tam metin bağlantısı DergiPark üzerinden sağlanmıştır.
DergiPark Kaydı ↗
✨

Yapay Zeka Hızlı Bakış & Çıkarımlar

AI Insight
⚡ TL;DR(1 Cümlede Hızlı Çıkarım)

Minimum bifilm density val-ue was measured at the same ultrasonic temperature and time.

📌 3 Maddede Bu Makale

🎯
Amaç & Hipotez:The aim of this study is to investigate the effect of ultrasonic treatment on the microstructural and mechanical properties of A356 aluminum al-loy.
📊
Temel Bulgular & Veri:Ultrasonic treatment was applied to 2 kg and 4 kg molten metals at different melting temperatures (700 oC, 720 oC and 740 oC) for different durations (0, 60, 180 and 300 seconds).
💡
Sonuç & Katkı:Minimum bifilm density val-ue was measured at the same ultrasonic temperature and time.
🔬Tür:Araştırma Makalesi
📍Kapsam:Genişletilmiş Akademik Örneklem
⚙️Değişkenler:Ultrasonic treatment · Aluminum alloy · Bifilm index

Abstract

The aim of this study is to investigate the effect of ultrasonic treatment on the microstructural and mechanical properties of A356 aluminum al-loy. Ultrasonic treatment was applied to 2 kg and 4 kg molten metals at different melting temperatures (700 oC, 720 oC and 740 oC) for different durations (0, 60, 180 and 300 seconds). Bifilm indices of the samples were also measured after all parameters were tested. The ultimate tensile strength (UTS) and elongation values were used to calculate the Quality Index (QI) of the samples. According to the results, the amount of liquid metal directly affects the the ultrasonic intensity that is produced during the treatment. Maximum UTS and elongation results were determined at 720 oC during 300 seconds for 4 kg casting. Minimum bifilm density val-ue was measured at the same ultrasonic temperature and time.

🔖

Bu Makaleye Atıf Yap

DOKUMACI, E., ÖNEL, K., AYBARÇ, U. (2022). Effect of Ultrasonic Treatment Parameters on Microstructural and Mechanical Properties of A356 Aluminum Alloy. International Journal of Automotive Science and Technology, Cilt: 4 - Sayı: 4, 234–243. https://ajindex.com/articles/540495

📄 Tam Metin PDF Okuyucu

📄

PDF görüntüleyici hazırlanıyor...

Kaynakça (13)

  1. H. Puga, M. Prokic, N. Van Donge: MMM Ultrasonic Metallurgy. http://mastersonics.com/documents/mmm_applications/ultrasonic_metallurgy/MMM-Ultrasonic-Metallurgy-Aluminium-International.pdf. Accessed 08 May 2018
  2. Birol, Y. (2013). Impact of grain size on mechanical properties of AlSi7Mg0.3 alloy: Materials Science and Engineering A, 559, 394–400.
  3. Nikanorov, S.P., Volkov, M. P., Gurin, V.N., Burenkov, Y. A., Derkachenko, L.I., Kardashev, B.K., Regel, L.L., Wilcox, W.R. (2005). Structural and mechanical properties of Al-Si alloys obtained by fast cooling of a levitated melt: Materials Science and Engineering:A, 390(1–2), 63–69.
  4. YE, H. (2003). An overview of the development of Al-Si-Alloy based material for engine applications: JMEPEG, 12(3), 288–297.
  5. Hawari, A. A., Khader, M., Hasan, W. E., Alijla, M., Manawi, A., Benamour, A. (2014). A life cycle assessment (LCA) of aluminum production process: International Journal of Mechanical, Aerospace, Industrial, Mechatronic and Manufacturing Engineering, 8(4), 704–710.
  6. Xu, H., Meek, T., Han, Q. (2007). Effects of ultrasonic field and vacuum on degassing of molten aluminum alloy: Materials Letters, 61(4–5), 1246–1250.
  7. Xu, H., Jian, X., Meek, T. T., Han, Q. (2004). Degassing of molten aluminum A356 alloy using ultrasonic vibration: Materials letters, 58(29), 3669–3673.
  8. Felberbaum, M., Landry-Désy, E., Weber, L., Rappaz, M. (2011). Effective hydrogen diffusion coefficient for solidifying aluminium alloys: Acta Materialia, 59(6), 2302–2308.
  9. Dispinar, D., Akhtar, S., Nordmark, A., Sabatino, M.D., Arnberg, L. (2010). Degassing, hydrogen and porosity phenomena in A356: Materials Science and Engineering: A, 527(16–17), 3719–3725.
  10. Dispinar, D., Campbell, J. (2004). Critical assessment of reduced pressure test. Part 1: Porosity phenomena: International Journal of Cast Metals Research, 17(5), 280–286.
  11. Dispinar, D., Campbell, J. (2011). Porosity, hydrogen and bifilm content in: Materials Science and Engineering: A, 528(10–11), 3860–3865.
  12. Dispinar, D., Akhtar, S., Nordmark, A., Syvertsen, F., Sabatino, M.D., Arnberg, L. (2012). Correlation between mechanical properties and porosity distribution of A356 in gravity die casting and low pressure die casting: Advanced Materials Research. Trans Tech Publ, 445, 283–288.
  13. Eskin, D.G., Atamanenko, T.V., Zhang, L., Katgerman, L. (2010). On the mechanism of grain refinement by ultrasonic melt treatment in the presence of transition metals: Essential Readings in Light Metals. 415–419. Eskin,