Microstructural Analysis of Austempered Ductile Iron Castings

Amaç & Hipotez:A ustempered ductile iron ADI castings have a wide range of application areas in engineering designs due to their promising mechanical properties and lower cost.

📊

Temel Bulgular & Veri:In a more detailed manner, the first locally produced ADI which cannot satisfy the mechanical properties stated in ISO 17804 is compared with the original sample which is conform with the standard.

💡

Sonuç & Katkı:In other words the relation between the macro mechanical properties and the microstructural conditions are tried to be clarified

🔬Tür:Araştırma Makalesi

📍Kapsam:Genişletilmiş Akademik Örneklem

⚙️Değişkenler:Austempered Ductile Iron · Mechanical properties · Microstructure

Abstract

A ustempered ductile iron ADI castings have a wide range of application areas in engineering designs due to their promising mechanical properties and lower cost. ADI has very good strength and toughness values at the same time its ductility is relatively high compared to most of the other cast irons. These promising mechanical properties originate from combination of specific graphite and matrix microstructure. The size, shape and fraction of graphite as well as the matrix microstructure influences the mechanical properties. In this paper the efforts regarding to a localization project of ADI is presented. In a more detailed manner, the first locally produced ADI which cannot satisfy the mechanical properties stated in ISO 17804 is compared with the original sample which is conform with the standard. The two pieces are inspected by mechanically and microstructurally by means of which necessary actions are detected for the local production. In other words the relation between the macro mechanical properties and the microstructural conditions are tried to be clarified

Anahtar kelimeler

Austempered Ductile Iron Mechanical properties Microstructure Graphite Nodularity

🔖

Bu Makaleye Atıf Yap

DAVUT, K., ÇETIN, B., ARSLAN, E., MECO, H., UZUN?, M. C. (2022). Microstructural Analysis of Austempered Ductile Iron Castings. Hittite Journal of Science and Engineering, Cilt: 3 - Sayı: 1, 29–34. https://ajindex.com/articles/538085

📄 Tam Metin PDF Okuyucu

Yeni Sekmede Aç ↗

↗Yeni Sekme

📄

PDF görüntüleyici hazırlanıyor...

Kaynakça (3)

ASM Handbook Volume 15: Casting, 2008,
Materials Park, Ohio, USA 2. Cast Metals Development Ltd. Austempered DuctileIron Castings - Advantages, Production, Properties and Specifications. Materials & Design 13 5 (1992) 285-297. 3. F. Kolcke, Arft M, Lung D. Material-Related Aspects of the Machinability of Austempered Ductile Iron. Springer. 4 (2010) 433-411. 4. Putatunda S.K, Kesani S, Tackett R, Lawes G. Development of Austenite Free ADI (Austempered Ductile Cast Iron). Materials Science and Engineering A 435–436 (2006) 112– 122. 5. Zimba J, Simbi D.J, Navara E. Austempered Ductile Iron: An Alternative Material for Earth Moving Components. Cement & Concrete Composites 25 (2003) 643–649. 6. Dhanasekaran S, Vadiraj A, Balachandran G, Kamaraj M. Mechanical Behaviour of an Austempered Ductile Iron. 63 5 (2010) 779-785. 7. Guo X.L, Su H.Q, WU B.Y, LIU Z.G. Characterization of Microstructural Morphology of ADI by Electron Microscopy. Microscopy Research and Technique 40 (1998) 336-340. 8. Janowak J.F., Norton P.A. A Guide To Mechanical Properties Possible By Austempering, 1.5% Ni, 0.3% Mo Iron. AFS Trans. 88 (1985) 123–135. 9. Putatunda S.K. Development of Austempered Ductile Cast Iron (ADI) With Simultaneous High Yield Strength And Fracture Toughness By A Novel Two-Step Austempering Process. Materials Science and Engineering A 315 (2001) 70–80 10. Trudel A., Gagné M., “Effect of Composition and Heat Treatment Characteristics of Austempered Ductile Irons”, Canadian Metallurgical Quarterly: The Canadian Journal of Metallurgy and Materials Science 36 (1997) 289 – 298 11. ASM Speciality Handbook: Cast Irons, Edited by Joseph R. Davis, ASM International 1996,
Materials Park, Ohio, USA 12. Bahmani M., Elliott R., Varahram N., “The Austempering Kinetics and Mechanical Properties of an Austempered Cu-Ni-Mo-Mn alloyed Ductile Iron”, Journal of Materials Science 32 (1997) 4783 - 4791 13. Aranzabal J., Gutierrez I., Rodriguez-Ibabe J.M., Urcola J.J., “Influence of the Amount and Morphology of Retained Austenite on the Mechanical Properties of an Austempered Ductile Iron”, Metallurgical and Materials Transactions A 28A (1997) 1143-1156 14. Aranzabal J., Gutierrez I., Urcola J.J, “Influence of Heat Treatments on Microstructure of Austempered Ductile Iron”, Materials Science and Technology 10 (1994) 728 – 737 15. Shanmugam P., Rao P.P., Udupa K.R., Venkataraman N., “Effect of Microstructure on the Fatigue Strength of an Austempered Ductile Iron”, Journal of Materials Scie