Itwas concluded that the abrasion resistance in the high hardness sample does not mean that it will be gooddue to the high hardness.
📌 3 Maddede Bu Makale
🎯
Amaç & Hipotez:The aim of this study was to improve the surface properties of the X6Cr17 ferritic stainless steels bycoating with the Al2O3-TiO2 powders in the thickness of 0-100µm, 100-200µm and 200-300µm by usingthe plasma spray method, one of thermal spray methods.
📊
Temel Bulgular & Veri:The tests were carried out by pin-on-disc method according to ASTM G133standard.
💡
Sonuç & Katkı:Itwas concluded that the abrasion resistance in the high hardness sample does not mean that it will be gooddue to the high hardness.
🔬Tür:Araştırma Makalesi
📍Kapsam:3 sample
⚙️Değişkenler:Alan Parametreleri
Abstract
The aim of this study was to improve the surface properties of the X6Cr17 ferritic stainless steels bycoating with the Al2O3-TiO2 powders in the thickness of 0-100µm, 100-200µm and 200-300µm by usingthe plasma spray method, one of thermal spray methods. Wear resistance of the samples was investigatedafter the coating process. The tests were carried out by pin-on-disc method according to ASTM G133standard. After examination of the results, it was observed highest abrasion resistance of A3 sample. Itwas concluded that the abrasion resistance in the high hardness sample does not mean that it will be gooddue to the high hardness.
🔖
Bu Makaleye Atıf Yap
DURMUŞ, H., TÜRKMEN, M., ÇALIGÜLÜ, U. (2022). Wear Resistances of X6Cr17 Ferritic Stainless-Steel Surfaces Coated with Al2O3 Powders Using Thermal Spray Method. Dicle Üniversitesi Mühendislik Fakültesi Mühendislik Dergisi, Cilt: 11 - Sayı: 3, 1167–1173. https://ajindex.com/articles/487575
Taskin M.; Caligulu U.; Kolukisa S. The effect of welding speed on the laser welding of X6Cr17 Ferritic stainless steel with AISI 1010 low Carbon steels. Practical Metallography 2009, 46, 11, pp. 598-607
Akın, U. Investigation of Wear Behavior of Ceramic and Ceramic-Polymer Coatings Coated with Thermal Spray Method on Aluminum Base, Master Thesis, Istanbul Technical University, Institute of Science and Technology, 2003
Davis, J.R. Thermal Spray Processes, Handbook of Thermal Spray Technology, International ASM, 329. ASM İnternational, USA, 2004
Aran, A.; Temel, M.A. Production, Use and Standards of Stainless Steels, Saritas Technical Publication, Istanbul, 2004
Kambur, K., The Effect of Different Substrate Temperatures on Coating Properties in Coating of Ti6Al4V alloy with HA. Master's thesis, Manisa Celal Bayar University, Turkey, 2018
Durmuş H; Çömez N; Gül C; Yurddaşkal M. Farklı Kimyasal İçeriğe Sahip Tellerin İki Pasolu Sert Dolgulu Malzemelerin Aşınma Davranışına Etkileri. Muş Alparslan Üniversitesi Fen Bilimleri Dergisi. 2018; 6(2): 561-564
AWS Committee, Thermal Spraying: Practice, Theory, and Application, American Welding Society Inc, 12-15, 1997
Hidalgo, V.H.; Varela, F.J.B.; Martinez, S.P. A comparative study of high-temperature erosion wear of plasma sprayed NiCrBSiFe and WC-NiCrBSiFe coatings under simulated coal-fired boiler conditions, Tribology International, 2001, 24, 161–169
Islak,S.; Ozorak, C.; Kucuk, O.; Akkas, M.; Sezgin, C. Microstructure and Hardness Properties of high velocity oxygen fuel (HVOF) Sprayed WCCo-SiC Coatings, Kastamonu University, Journal of Engineering and Science, 2015, Vol.1, pp. 1– 7
Rajarathnam D. R. P.; Jayaraman M. Investigation of the wear behaviour of an AISI 1040 forged steel shaft with plasmaspray ceramic-oxide coatings for sugar-cane mills. Materiali in tehnologije, 2017. 51(6), 939-944
Sert, Y., Examining Wear Properties of Textile Piece Coated with Plasma Spray Technique, Master's thesis, Sakarya University Institute of Science, Sakarya, 2007
Aslan O., Examining Corrosion Behaviors of Single and Double layered AISI 316L Stainless Steel Coated by Plasma Spray Coating, Afyon Kocatepe University, Afyon, 2015
Islak, S; Özorak, C; Eski, Ö. Plazma Sprey Yöntemiyle AISI 304 Paslanmaz Çelik Üzerinde Üretilen Ti3SiC2 MAX Fazlı Kaplamanın Karakterizasyonu. Bitlis Eren Üniversitesi Fen Bilimleri Dergisi, 2019, 8 (1), 206-213. DOI: 10.17798/bitlisfen.45308