Isıl İşlem Görmüş Ahşap Kullanılarak Çeşitli Koşullar Altında Yapışma Performansının İncelenmesi

An Investigation of Adhesion Performance Under Various Conditions Using Heat-Treated Wood

Mustafa ALTUNOK
Sayfa
711–714
Yayın Tarihi
2021-06-01
DOI
—
🏛️Bu makalenin bibliyografik verileri ve tam metin bağlantısı DergiPark üzerinden sağlanmıştır.
DergiPark Kaydı ↗
✨

Yapay Zeka Hızlı Bakış & Çıkarımlar

AI Insight
⚡ TL;DR(1 Cümlede Hızlı Çıkarım)

It was observed that the samples that were kept under A1 conditions and tested had wood rupture (error) between 70% and 100%, and the samples tested after holding in A4 and A5 conditions mostly broke off from the glue joint.

📌 3 Maddede Bu Makale

🎯
Amaç & Hipotez:In this study, the adhesion performance of oak (Quercus petrea Liebl.) And Scotch pine (Pinus Silvestris L.) wood samples that were heat treated and glued with 1K-PUR adhesive were kept under different conditions (A1-A4-A5) and moisture contents (20°C /% 35, 20°C /%65 ve 20°C /% 95), and then the adhesion performance was investigated.Rough sized pieces of both types of wood were heat treated at 195°C for 2 hours.
📊
Temel Bulgular & Veri:Test samples were prepared from untreated and heat treated blanks (DIN EN 204).
💡
Sonuç & Katkı:It was observed that the samples that were kept under A1 conditions and tested had wood rupture (error) between 70% and 100%, and the samples tested after holding in A4 and A5 conditions mostly broke off from the glue joint.
🔬Tür:Araştırma Makalesi
📍Kapsam:Genişletilmiş Akademik Örneklem
⚙️Değişkenler:Heat treatment · holding environment · moisture content

Abstract

In this study, the adhesion performance of oak (Quercus petrea Liebl.) And Scotch pine (Pinus Silvestris L.) wood samples that were heat treated and glued with 1K-PUR adhesive were kept under different conditions (A1-A4-A5) and moisture contents (20°C /% 35, 20°C /%65 ve 20°C /% 95), and then the adhesion performance was investigated.Rough sized pieces of both types of wood were heat treated at 195°C for 2 hours. Test samples were prepared from untreated and heat treated blanks (DIN EN 204). Tensile tests according to DIN EN 204 were applied to samples kept at 20°C/35%, 20°C/65% and 20°C/95% temperature and relative humidity, respectively, and the adhesion performance was determined in three climatic conditions.At the end of these tests, it was found that the holding environment and climatic conditions have a significant effect on the adhesion resistance. It was observed that the samples that were kept under A1 conditions and tested had wood rupture (error) between 70% and 100%, and the samples tested after holding in A4 and A5 conditions mostly broke off from the glue joint.

🔖

Bu Makaleye Atıf Yap

ALTUNOK, M. (2021). Isıl İşlem Görmüş Ahşap Kullanılarak Çeşitli Koşullar Altında Yapışma Performansının İncelenmesi. Politeknik Dergisi, Cilt: 24 - Sayı: 2, 711–714. https://ajindex.com/articles/422347

📄 Tam Metin PDF Okuyucu

📄

PDF görüntüleyici hazırlanıyor...

Kaynakça (14)

  1. Vanya, C. “Damage problems in glued laminated timber”, Drewno. Pr. Nauk. Donies. Komunik, 55(188):115-128, (2012)
  2. Eckelman, C. A. “The shrinking and swelling of wood and its effect on furniture.” Purdue University Cooperative Extension Service. Pub. FNR 163. West Lafayette, IN (1998)
  3. Dietsch, P., Franke, S., Franke, B., Gamper, A., Winter, S., “Methods to determine wood moisture content and their applicability in monitoring concepts.” Journal of Civil Structural Health Monitoring, 5(2): 115–127, (2015)
  4. Volkmer, T., Schmidt, J.A., Kranitz, K., Niemz, P., “Untersuchungen zum Einfluss der Klebstoffart auf den Diffusionswiderstand von Holzverklebungen.” Bauphysik, 34 (2): 55-60, (2012)
  5. Altunok, M., Wetzig, M., Niemz, P., “Verklebtes Thermoholz im Feuchtraum verwenden: Einfluss won Wärmebehandlung, Holzfeuchte und Prüflagerfolge auf die Zugescherfestigkeit von 1K-PUR Verbindungen”, Holz-Zentralblatt, Stuttgart, 20: 519-520, (2012)
  6. Elstermann, F., “Einfluss der Oberflächenqualität des Holzes auf die Verklebungsgüte.” Dresden: Berufsakademie Sachsen, Staatliche Studienakademie Dresden, Holztechnik, Dissertation/Diplomarbeit (2011)
  7. Hering, S., “Charakterisierung und Modellierung der Materialeigenschaften von Rotbuchenholz zur Simulation von Holzverklebungen.” DISS. ETH Nr. 19903, ETH Zürich (2011)
  8. Clad W., “Über das Wesen einer Verklebung und die Fugenelastizität ausgehärteter Leimfugen bei Holzverleimungen. Dissertation”, Technische Hochschule Stuttgart (1964)
  9. Brockmann W., Geiß P.L., Klingen, J., Schröder, B.: Klebtechnik: Klebstoffe, Anwendungen und Verfahren, WILEY-VCH (2005)
  10. Clauß S., Joscak M., Niemz, P., “Thermal stability of glued wood joints measured by shear tests.”, European Journal of Wood and Wood Products, 69(1): 101-111, (2011a)
  11. Clauß S., Dijkstra D.J., Gabriel J., Kläusler O., Matner M., Meckel W. Niemz P., “Influence of the chemical structure of PUR prepolymers on thermal stability.”, International Journal of Adhesion and Adhesives, 31(6): 513-523, (2011b)
  12. Sahin Kol H., Ozbay G., Altun S., “Shear strength of heat-treated tali (Erythrophleum ivorense) and iroko (Chlorophora excelsa) woods, bonded with various adhesives.”, BioResources, 4(4): 1545–1554, (2009)
  13. Dilik T. Hiziroglu S., “Bonding strength of heat treated compressed Eastern redcedar wood.”, Materials and Design, 42: 317–320, (2012)
  14. Esteves B. Pereira H., “Wood modification by heat treatment: A review.” BioResources,