Evaluation of low-velocity impact behavior of epoxy nanocomposite laminates modified with SiO2 nanoparticles at cryogenic temperatures

Ahmet C. TATAR
Halil B. KAYBAL
HASAN ULUS
OKAN DEMİR
AHMET AVCI
Sayfa
115–125
DOI
—
🏛️Bu makalenin bibliyografik verileri ve tam metin bağlantısı DergiPark üzerinden sağlanmıştır.
DergiPark Kaydı ↗
✨

Yapay Zeka Hızlı Bakış & Çıkarımlar

AI Insight
⚡ TL;DR(1 Cümlede Hızlı Çıkarım)

Moreover, the peak contact forces are reduced in low-temperature conditions.

📌 3 Maddede Bu Makale

🎯
Amaç & Hipotez:Epoxy based fiber reinforced composites are widely utilized in aerospace applications due to mechanical properties, thermal stability and, chemical resistance.
📊
Temel Bulgular & Veri:The LVI tests were conducted at RT (room temperature), 0 °C, -50 °C, -150 °C and -196 °C (liquid nitrogen temperature) on the composite laminates to measure influence on their energy absorption capacity.
💡
Sonuç & Katkı:Moreover, the peak contact forces are reduced in low-temperature conditions.
🔬Tür:Araştırma Makalesi
📍Kapsam:Genişletilmiş Akademik Örneklem
⚙️Değişkenler:Alan Parametreleri

Özet

Epoxy based fiber reinforced composites are widely utilized in aerospace applications due to mechanical properties, thermal stability and, chemical resistance. However, it is known that materials become brittle and due to the poor crack resist restricts their applications in cryogenic engineering applications. The purpose of this paper is to experimentally investigate the cryogenic temperatures’ effect on the low-velocity impact (LVI) test of composite laminates. In addition, the effect of matrix modification in the studied composites was investigated. The LVI tests were conducted at RT (room temperature), 0 °C, -50 °C, -150 °C and -196 °C (liquid nitrogen temperature) on the composite laminates to measure influence on their energy absorption capacity. LVI tests performed according to ASTM-D-7136 standard under 10, 20 and 30 J impact energy levels. The results show that the contact forces and energy absorption capacities are improved by adding SiO2 nanoparticles into the epoxy matrix. The absorbed energy at cryogenic temperatures is increased by 24.87% from 18.1 J of pure epoxy resin to 22.7 J of modified epoxy. For the purpose of comparison, the LVI properties of composites at room temperature (RT) are also investigated. It is noted that the energy absorption capacity is not higher at cryogenic temperatures than that at RT for the modified and neat epoxy composites. Moreover, the peak contact forces are reduced in low-temperature conditions.

🔖

Bu Makaleye Atıf Yap

TATAR, A. C., KAYBAL, H. B., ULUS, H., DEMİR, O., AVCI, A. (2019). Evaluation of low-velocity impact behavior of epoxy nanocomposite laminates modified with SiO2 nanoparticles at cryogenic temperatures. Research on Engineering Structures and Materials, Cilt: 5 - Sayı: 2, 115–125. https://ajindex.com/articles/302699

📄 Tam Metin PDF Okuyucu

📄

PDF görüntüleyici hazırlanıyor...

Kaynakça (7)

  1. Kagitci, Y.C. and N. Tarakcioglu, The effect of weld line on tensile strength in a polymer composite part. The International Journal of Advanced Manufacturing Technology, 2016. 85(5-8): p. 1125-1135.
  2. Guermazi, N., et al., Investigations on the fabrication and the characterization of glass/epoxy, carbon/epoxy and hybrid composites used in the reinforcement and the repair of aeronautic structures. Materials & Design (1980-2015), 2014. 56: p. 714-724.
  3. El Moumen, A., et al., Dynamic properties of carbon nanotubes reinforced carbon fibers/epoxy textile composites under low velocity impact. Composites Part B: Engineering, 2017. 125: p. 1-8.
  4. Bansemir, H. and O. Haider, Fibre composite structures for space applications—recent and future developments. Cryogenics, 1998. 38(1): p. 51-59. https://doi.org/10.1016/S0011-2275(97)00110- 0 [5] Praveen, R., et al., Hybridization of carbon–glass epoxy composites: An approach to achieve low coefficient of thermal expansion at cryogenic temperatures. Cryogenics, 2011. 51(2): p. 95-104.
  5. Hartwig, G. and S. Knaak, Fibre-epoxy composites at low temperatures. Cryogenics, 1984. 24(11): p. 639-647.
  6. Kim, M.-G., J.-B. Moon, and C.-G. Kim, Effect of CNT functionalization on crack resistance of a carbon/epoxy composite at a cryogenic temperature. Composites Part A: Applied Science and Manufacturing, 2012. 43(9): p. 1620-1627.
  7. Timmerman, J.F., et al., Matrix and fiber influences on the cryogenic microcracking of carbon fiber/epoxy composites. Composites Part A: Applied Science and Manufacturing, 2002. 33(3): p. 323-329. https://doi.org/10.1016/S1359- 835X(01)00126-9 [9] Salehi-Khojin, A., et al., The role of temperature on impact properties of Kevlar/fiberglass composite laminates. Composites Part B: Engineering, 2006. 37(7-8): p. 593-602. https://doi.org/10.1016/j.compositesb.2006.03.009 [10]Icten, B.M., et al., Low temperature effect on impact response of quasi-isotropic glass/epoxy laminated plates. Composite Structures, 2009. 91(3): p. 318-323. https://doi.org/10.1016/j.compstruct.2009.05.010 [11]Deng, S., L. Ye, and K. Friedrich, Fracture behaviours of epoxy nanocomposites with nano-silica at low and elevated temperatures. Journal