Amaç & Hipotez:In this study, instead of clay the effect of trass - which is used as a component for clinker production in the cement industry and has properties that are significant for agriculture - are researched.
📊
Temel Bulgular & Veri:The clinkering properties of raw material compositions which are prepared according to the constant Lime Saturation Factor (LSF) degree were considered in relation to sintering at fixed temperature (1450 oC).
💡
Sonuç & Katkı:Because of the C3S phases are 70,43 % and 42,72 % respectively.
In this study, instead of clay the effect of trass - which is used as a component for clinker production in the cement industry and has properties that are significant for agriculture - are researched. The clinkering properties of raw material compositions which are prepared according to the constant Lime Saturation Factor (LSF) degree were considered in relation to sintering at fixed temperature (1450 oC). Two different clinkers - namely trass 1 which is added to clinker 1 and trass 2 which is added to clinker 2 - were produced from the raw material compositions prepared at a constant LSF. The clinkering reaction was determined by the measurement of the free CaO (FCaO) value. According to the FCaO content and the amount of C3S test results, clinker 1 is preferable to clinker 2. Because of the C3S phases are 70,43 % and 42,72 % respectively.
TASCI, E., AKTAS, M., YILMAZ, B., ISIK, İ. (2014). The Effects of Addition Two Different Types of Trass to the Clinkering Reaction. Gazi University Journal of Science, Cilt: 27 - Sayı: 1, 701–708. https://ajindex.com/articles/255277
Worrell, E., Martin, N., Price, L., “Potentials for energy efficiency improvement in the US cement industry”, Energy 2000, 25: 1189(2000).
Mehta, P.K., “Greening of the concrete industry for sustainable development”, Concrete International 2002, 24-23(2002). Aída, Z., Pedro, B., “Low temperature preparation of belitic cement clinker”, Journal of the European Ceramic Society, 29: 1879–1885(2009).
Uzal, B., Turanlı, L., “Studies on blended cement containing a high volume of natural pozzolans”, Cement and Concrete Research, 33:1777–81(2003).
Rodriguez-Camacho, R.E., “Importance of using natural pozzolans on concrete durability”, Cement and Concrete Research, 32: 1851–1858 (2002).
Uribe-Afif, R., Colak, A., “The long-term durability performance of gypsum – Portland cement – natural pozzolan blends”, Cement and Concrete Research, 32: 109– 115(2002).
Vu, D., Stroeven, P., Bui, V., “Strength and durability aspects of calsined caolin-blended Portland cement mortar and concrete”, Cement and Concrete Composition, 23: 471–478 (2001).
Cavdar, A., Yetgin, S., “Tane inceliğinin traslı çimento özelliklerine etkisi”, In: Ergin A, Özdemir G, editors, Türkiye Inşaat Mühendisliği XVII. Teknik Kongresi, Istanbul, 451–454(2004).
Yetgin, S., Cavdar, A., “Tras Oranı Değisiminin Traslı Çimentonun Bazı Özelliklerine Etkisi”, In: Özturan Tet al., editors, Advances in Civil Engineering 2004 6th International Conference., Istanbul, 1084–1092(2004).
Canpolat, F., Yılmaz, K., Köse, M., Sumer, M., Yurdusev, M., “Use of zeolite, coal bottom ash and fly ash as replacement materials in cement production”, 2325(2003). Concrete, 2324 Shannag, M., “High strength concrete containing natural pozzolan and silica fume”, Cement and Concrete Composition, 22: 399–406(2000).
Turanlı, L., Uzal, B, Bektas, F., “Effect of large amounts of natural pozzolan addition on properties of blended cements”, Cement and Concrete Research, 35(6):1106–1111(2005).
Türkmenoğlu, A.G., Tanku, A., “Use of tuffs from central Turkey as admixture in pozzolanic cements assessment of their petrographical properties”, Cement and Concrete, 629–637(2002).
Cavdar, A., Yetgin, S., “Availability of tuffs from northeast of Turkey as natural pozzolan on cement”, Construction and Building Materials, 21:2066– 2071(2007). TS EN 196-6, “Methods of testing cement-Part 6: Determination of fineness”, Turkish standard according to European Norms, Ankara (2002). TS EN 196-2, “Methods of testing cement-Part 2: Chemical Analysis of Cement”, Tur