Polipropilen Bazlı Dk1 Nanokil Kompozitlerinin Elektret Özellikleri

Electret Properties of Dk1 Nanoclay Composites Based on Polypropylene

Aynura Hadiyeva(Azerbaijan State Oil and Industry University)0000-0001-7238-1066
Arzu Sadigova(Institute of Physics, Ministry of Science and Education of Azerbaijan,)0000-0002-8536-9688
Parvana Asilbeyli(Institute of Physics, Ministry of Science and Education of Azerbaijan,)0009-0003-8093-2464
Vilayet Alekberov(Institute of Physics, Ministry of Science and Education of Azerbaijan,)0009-0003-8093-4464
Sayfa
1–5
Yayın Tarihi
2026-03-29
🏛️Bu makalenin bibliyografik verileri ve tam metin bağlantısı DergiPark üzerinden sağlanmıştır.
DergiPark Kaydı ↗
✨

Yapay Zeka Hızlı Bakış & Çıkarımlar

AI Insight
⚡ TL;DR(1 Cümlede Hızlı Çıkarım)

Tp artdıqca, σef′nin maksimum değerleri küçük Ep değerlerinde gözlenilir.

📌 3 Maddede Bu Makale

🎯
Amaç & Hipotez:Polipropilen (PP) ve buna dayalı farklı yüzdelerde Dk1 marka nanokil içeren nanokil nanokompozitlerin elektret özellikleri farklı sıcaklıklarda ve polarizasyon voltajlarında incelenmiştir.
📊
Temel Bulgular & Veri:Elde edilen elektret malzemelerdeki biriken yüklerin etkin yüzey yoğunluğu (σef), Dk1 miktarına bağlıdır.
💡
Sonuç & Katkı:Tp artdıqca, σef′nin maksimum değerleri küçük Ep değerlerinde gözlenilir.
🔬Tür:Araştırma Makalesi
📍Kapsam:Genişletilmiş Akademik Örneklem
⚙️Değişkenler:nanokil · nanokompozit · elektret

Özet

Polipropilen (PP) ve buna dayalı farklı yüzdelerde Dk1 marka nanokil içeren nanokil nanokompozitlerin elektret özellikleri farklı sıcaklıklarda ve polarizasyon voltajlarında incelenmiştir. Elde edilen elektret malzemelerdeki biriken yüklerin etkin yüzey yoğunluğu (σef), Dk1 miktarına bağlıdır. Dk1 arttıkça σef artmakta ve %10'dan sonra azalma görülmektedir. %10'ı aşan katkı maddesi miktarıyla elektret özelliklerinin bozulması, nanokompozitlerin kümeleşmesiyle açıklana bilir. PP′ye eklenen Dk1 parçacıklar da makrodipollar gibi davranır, dipol gevşeme süreçlerinin meydana gelmesiyle kendini gösterir. Elektrotermopolerizasiyadan sonar elektret malzemelerin σef′si Tp ve Ep′ye bağlıdır. Tp artdıqca, σef′nin maksimum değerleri küçük Ep değerlerinde gözlenilir.

Abstract

The electret properties of polypropylene (PP) and nanoclay nanocomposites containing various percentages of Dk1 brand nanoclay were investigated at different temperatures and polarization voltages. The effective surface density (σef) of the accumulated charges in the resulting electret materials depends on the amount of Dk1. σef increases as Dk1 increases, and a decrease is observed after 10%. The deterioration of electret properties with additive amounts exceeding 10% can be explained by the aggregation of the nanocomposites. Dk1 particles added to PP also behave like macrodipoles, manifesting themselves through dipole relaxation processes. After electrothermopolarization, the σef of electret materials depends on Tp and Ep. As Tp increases, maximum values of σef are observed at small values of Ep.

🔖

Bu Makaleye Atıf Yap

Hadiyeva, A., Sadigova, A., Asilbeyli, P., Alekberov, V. (2026). Polipropilen Bazlı Dk1 Nanokil Kompozitlerinin Elektret Özellikleri. Politeknik Dergisi, Cilt: 29 Sayı: 3, 1–5. https://doi.org/10.2339/politeknik.1758543

📄 Tam Metin PDF Okuyucu

📄

PDF görüntüleyici hazırlanıyor...

Kaynakça (22)

  1. A. Kravtsov, H. Brünig, S. Zhandarov, R. Beyreuther. Advances in Polymer Technology, 19(4):312–316 (2000).
  2. A. G. Kravtsov. Plasticheskiye Massy, 8:6–10 (2000).
  3. N. V. Kestelman, L. S. Pinchuk, V. A. Goldade. “Electrets in Engineering: Fundamentals and Applications.” Kluwer Academic Publishers, Boston, p. 281, (2000).
  4. A. Rychkov, D. Rychkov. “Publishing House of Russian State Pedagogical University named after A.I. Herzen”, pp. 47–62 (2009).
  5. D. A. Rychkov, A. E. Kuznetsov, A. A. Rychkov. “St. Petersburg: Publishing House of Russian State Pedagogical University named after A.I. Herzen”, p. 159 (2013).
  6. M. Yu. Vasilkov, E. A. Busygina, L. V. Nikitina, I. D. Kosobudsky. Vestnik SQTU, No. 2, pp. 72–76 (2014).
  7. E. Giannelis. Advanced Materials, Vol. 8:29–35 (1995).
  8. E. Giannelis, N. Krishnamoorti, E. Manias. Advances in Polymer Science, Vol. 138:107–147 (1999).
  9. L. McCarty, G. Whitesides. Angewandte Chemie, Vol. 47:2188–2207 (2008).
  10. M. Kovalenko, V. Goldade. International Forum: Problems and Scientific Solution (2021).
  11. Kh. S. Aliev, M. M. Kuliev, R. S. Ismailova, B. A. Mamedov, N. Sh. Aliev. Surface Engineering and Applied Electrochemistry, 52(5):494–498 (2016).
  12. M. M. Kuliyev, A. M. Magerramov, R. S. Ismayilov, A. A. Nabiyev. Perspektivniye Materiali, 9:17–22 (2015).
  13. M. F. Galikhanov, D. A. Yeremeyev, R. Ya. Deberdeyev. Plasticheskiye Massy, No. 10, pp. 26–28 (2002).
  14. A. A. Rychkov, A. A. Malygin, S. A. Trifonov, D. A. Rychkov. Journal of Applied Chemistry, 77(2):280–284 (2004).
  15. Y. A. Gorokhovatsky, I. Y. Gorokhovatsky. Proceedings of the Herzen State Pedagogical University, No. 95, pp. 63–67 (2009).
  16. A. A. Rychkov, V. N. Pak, A. E. Kuznetsov. Proceedings of the Herzen State Pedagogical University, No. 26, pp. 137–141 (2007).
  17. D. A. Eremeev, M. F. Galikhanov, R. Ya. Deberdeev. Structure and Dynamics of Molecular Systems, Part 1, Issue 10, pp. 122–125 (2003).
  18. M. M. Kuliev, R. S. Ismailova. Surface Engineering and Applied Electrochemistry, 46(5):447–451 (2010).
  19. N. Mohmeyer, N. Behrendt, X. Zhang. Polymer, 48(6): 1612–1619 (2007).
  20. A. Viraneva, T. Yovcheva, I. Bodurov, et al. Bulgarian Chemical Communications, 45(B):73–76 (2013).
  21. A. Berghout, D. Tunega, A. Zaoui. Clays and Clay Minerals, Vol. 58, pp. 174–187 (2010).
  22. M. Alexandre, P. Dubois. Materials Science and Engineering: R: Reports, Vol. 28, pp. 1–63 (2000).