FABRICATION OF TERNARY SILICA-CALCIUM-MAGNESIUM AEROGELS: EFFECT OF FEEDING RATE AND MOLAR RATIO ON PROPERTIES

Burcu KARAKUZU İKİZLER
Pınar TERZİOĞLU
Tülay Merve TEMEL SOYLU
Sevil YÜCEL
Sayfa
905–915
Yayın Tarihi
2023-12-01
DOI
—
🏛️Bu makalenin bibliyografik verileri ve tam metin bağlantısı DergiPark üzerinden sağlanmıştır.
DergiPark Kaydı ↗
✨

Yapay Zeka Hızlı Bakış & Çıkarımlar

AI Insight
⚡ TL;DR(1 Cümlede Hızlı Çıkarım)

The resultant aerogels are promising candidates as adsorbents to remove various contaminants.

📌 3 Maddede Bu Makale

🎯
Amaç & Hipotez:The silica-calcium-magnesium ternary aerogels were prepared by a solvent exchange method and a subsequent ambient pressure drying process.
📊
Temel Bulgular & Veri:The effect of process parameters such as feeding rate (9-70 mL.min-1) and molar ratio (Si/(Ca:Mg) = 1:1 - 3:1) on the material characteristics including density, elemental content, surface area, pore size, pore volume, and morphology of powders were investigated.
💡
Sonuç & Katkı:The resultant aerogels are promising candidates as adsorbents to remove various contaminants.
🔬Tür:Araştırma Makalesi
📍Kapsam:Genişletilmiş Akademik Örneklem
⚙️Değişkenler:Ambient pressure drying · Co-doped silica · Pore structure

Abstract

The silica-calcium-magnesium ternary aerogels were prepared by a solvent exchange method and a subsequent ambient pressure drying process. The effect of process parameters such as feeding rate (9-70 mL.min-1) and molar ratio (Si/(Ca:Mg) = 1:1 - 3:1) on the material characteristics including density, elemental content, surface area, pore size, pore volume, and morphology of powders were investigated. Aerogels were characterized by Fourier transform infrared spectroscopy (FTIR), inductively coupled plasma optical emission spectroscopy (ICP-OES), scanning electron microscopy (SEM), Brunauer–Emmett–Teller (BET), Barrett–Joiner–Halenda (BJH) and tapping density analysis. It was found that the molar ratio of Si/(Ca:Mg) could remarkably affect the surface area and density of aerogels, while the feeding rate had slight effect. The resultant aerogels exhibited high specific surface areas. The results showed that the aerogel has a Si/(Ca:3Mg) molar composition obtained with 9 mL.min-1 had the highest surface area (524 m2.g−1). The increase of Ca to Mg molar ratio caused a decrease in the surface area and density of samples. The resultant aerogels are promising candidates as adsorbents to remove various contaminants.

🔖

Bu Makaleye Atıf Yap

İKİZLER, B. K., TERZİOĞLU, P., SOYLU, T. M. T., YÜCEL, S. (2023). FABRICATION OF TERNARY SILICA-CALCIUM-MAGNESIUM AEROGELS: EFFECT OF FEEDING RATE AND MOLAR RATIO ON PROPERTIES. Konya Journal of Engineering Sciences, Cilt: 11 Sayı: 4, 905–915. https://ajindex.com/articles/1019253

📄 Tam Metin PDF Okuyucu

📄

PDF görüntüleyici hazırlanıyor...

Kaynakça (10)

  1. T. Zhou, X. Cheng, Y. Pan, C. Li, L. Gong, and H. Zhang, “Mechanical performance and thermal stability of glass fiber reinforced silica aerogel composites based on co-precursor method by freeze drying,” Applied Surface Science, vol. 437, pp. 321–328, 2018.
  2. F. Pan, B. Zhang, Y. Ding, L. Wang, F. Xie, W. Cai, S. Liu, and J. Zhou, “New composite aerogel-like adsorbents for thiophene based on π-complexation,” Separation and Purification Technology, 192, pp. 46–54, 2018.
  3. T. M. Temel, B. K. İkizler, P. Terzioğlu, S. Yücel, and Y. B. Elalmış, “The effect of process variables on the properties of nanoporous silica aerogels: an approach to prepare silica aerogels from biosilica,” Journal of Sol-Gel Science and Technology, vol. 84, no. 1, pp. 51–59, Jul. 2017. J. L. Mohanan and S. L. Brock, “Influence of Synthetic and Processing Parameters on the Surface Area, Speciation, and Particle Formation in Copper Oxide/Silica Aerogel Composites,” Chemistry of Materials, vol. 15, no. 13, pp. 2567–2576, May 2003.
  4. C. Zhao, Y. Li, W. Ye, X. Shen, X. Yuan, C. Ma, and Y. Cao, “Performance regulation of silica aerogel powder synthesized by a two-step Sol-gel process with a fast ambient pressure drying route,” Journal of Non-Crystalline Solids, vol. 567, pp.120923, Sep 2021.
  5. X. Wu, G. Shao, S. Cui, L. Wang, and X. Shen, “Synthesis of a novel Al2O3–SiO2 composite aerogel with high specific surface area at elevated temperatures using inexpensive inorganic salt of aluminum,” Ceramics International, vol. 42, no. 1, Part A, pp. 874–882, Jan. 2016.
  6. X. Hou, R. Zhang, and D. Fang, “Novel whisker-reinforced Al2O3–SiO2 aerogel composites with ultra-low thermal conductivity,” Ceramics International, vol. 43, no. 12, pp. 9547–9551, Aug. 2017.
  7. J. Yao, X. Gao, Y. Wu, X. Zhao, and X. Li, “High-temperature resistant ambient pressure-dried aluminum doped silica aerogel from inorganic silicon and aluminum sources.” Ceramics International, vol. 48, pp.15006-15016, Jun. 2022.
  8. S. Zhang, Z. Zhang, J. Pei, R. Li, J. Zhang, J. Cai, and J. Cui, “A novel TiO2-SiO2 aerogel nanocomposite absorbent: preparation, characterization and photocatalytic degradation effects on automobile exhaust,” Materials Research Express, vol. 5, no. 2, p. 025036, Feb. 2018.
  9. W. Zou, H. Bian, J. Guo, J. Xu and B. Guo, “Preparation of Titania–Silica Composite Aerogel at Atmospheric Pressure and Its Catalytic Performance in the Synthesis of Poly (Butylene Succinate)” Materials, vol 16, pp. 3296, Apr. 2023.
  10. G. Zu, J. Shen, L. Zou, W. Z