AI Summary & Key Takeaways
AI InsightThe CIE - LAB system was used for determining overall color change (AE'ab).
📌 3 Key Takeaways
Abstract
The effect of accelerated aging time on color stability of intrinsically and extrinsically stained porcelain used in metal - ceramic restorations was investigated in this study. Metal ceramic samples were made in disk form that were 15 mm in diameter and 2 mm thick. Four groups were made and each group contained ten samples. Black stain was applied directly to the opaque in the first group (opaque stained group). The second group was made with the black stain interposing between 0.5 mm of body porcelain below and 0.5 mm of the same porcelain above (dentin stained group). A layer of black stain was applied over the enamel porcelain and this was the third group (enamel stained group). The fourth group was not stained (nonstained group). Color measurements were made after 300, 600, and 900 hours of accelerated aging time. The CIE - LAB system was used for determining overall color change (AE'ab). Chroma changes (AC'ab) and hue differences (AH'ab) were determined. Kruskal - Wallis Variance Analysis and Friedman Tests were used for statistical comparisons for analyzing AE*ab, AC*ab, and AH*ab. Nonsignificant differences in AE'ab, AC'ab, and AH*ab values for any of the groups were found for different aging times. Color differences were determined according to NBS units for all groups for different aging times. Color diferences (NBS units) that were determined for the groups varied in the acceptable range of 0.17 to 1.66. Aging times have not important effect on color characteristics of intrinsically and extrinsically stained porcelain used in metal - ceramic restorations.
Özet
Bu çalışmada hızlı yaşlanma zamanının, metal seramik restorasyonlarda iç ve dış boyama yapılmış porselendeki renk stabilitesine etkisi araştırıldı. Her bir grup için disk şeklinde 10 örnek hazırlandı. İlk grupta, siyah boya doğrudan opak üzerine uygulandı. İkinci grupta,siyah boya aynı porselenin 0.5 mm üzerinde, 0.5 mm dentin porseleninin altında olacak şekilde araya uygulandı. Üçüncü grup için, bir tabaka siyah boya mine porseleninin üzerine uygulandı. Dördüncü grup boyanmadı. Renk ölçümleri 300, 600 ve 900 saat yaşlandırma sonrası yapıldı. Toplam renk değişimini (A E* ab) belirlemek için CIE LAB sistemi kullanıldı. Chroma (AC*ab) ve hue (AH*ab) değişimleri belirlendi. İstatistiksel kıyaslamalar için Kruskal Wallis Varyans analizi ve Friedman testleri kullanıldı. Gruplar için farklı yaşlanma zamanlarında AE*ab, AC*ab ve AH*ab değerlerinde önemsiz farklılıklar bulundu. Renk değişiklikleri NBS birimine göre belirlendi ve gruplar için kabul edilebilir düzeyde bulundu. Yaşlandırma zamanının iç ve dış boyama yapılmış metal seramik restorasyonların renk özelliklerine önemsiz etkisi vardı.