The purpose of this study is to investigate how a resin modified glass ionomer cement and polyacid modified glass resin composite is effected from ultrasonic sealing treatment. For this purpose 20 newly extracted human noncarious unrestorated maxillar 1..molar tooth were used. Standard Class V type cavities were prepared on the buccal surface of teeth in the depth of 3 mm's, width of 5 mm's and height of 4 mm's. Hytac and Vitremer were used according to the instructions of the manufacturer firm and ultrasonic tips used to the enamel and cement margins afterwards. Specimens were investigated with using SEM. Ultrasonic scaling treatment observed to effect the marginal integrity negatively as a result.
Özet
Bu çalışmanın amacı; bir rezin modifiye cam iyonomer siman (Vitremer, 3M, U.S.A) ile bir poliasit modifiye kompozit rezinin (Hytac, ESPE, GERMANY) ultrasonik plak temizleme işleminden ne yönde etkilendiğini incelemektir, Bu amaçla 20 adet yeni çekilmiş, çürüksüz, restorasyonsuz üst 1. Molar diş kullanıldı. Dişlerin bukkal yüzeyine 3 mm derinlikte, 4 mm yükseklikte, 5 mm eninde standart Cl V kaviteler hazırlandı. Hytac ve Vitremer üretici firma önerileri doğrultusunda uygulandıktan sonra ultrasonik uç mine ve sement üzerine uygulandı. Örnekler SEM' de incelendi. Sonuç olarak uygulamanın restorasyonların marjinal bütünlüğünü olumsuz etkilediği gözlendi