In this study, the recovery of surface properties of AISI 316 stainless steel was aimed by atmospheric plasma spray coating method. Two powder metal alloys with different chemical composition were used in order to investigate the change and development of surface properties. First powder mixture is 100 % woka (Ni 78-82% Cr 18-22) 7202, and the second one is composed of 50 % woka 7202 (Ni 78-82% Cr 18-22) and 50 % diamalloy 2002(Ni 66%-Cr 18%). The coated samples were exposed to microstructure investigations, microhardness measurements from surface to center, XRD, SEM and EDS analyses and the 2D and 3D surface roughness measurements were performed. In addition, all samples were exposed to wear test with different load and velocities by using alumina ball. The worn surfaces were detected by EDS and SEM analyses at the end of the wear test.
Özet
Bu çalışmada AISI 316 paslanmaz çeliğinin yüzey özelliklerinin atmosferik plazma sprey kaplama yöntemi kullanılarak iyileştirilmesi amaçlanmıştır. Yüzey özelliklerini gelişimini ve değişimini inceleyebilmek için iki farklı kimyasal içeriğe sahip toz kullanılmıştır. Birincil toz karışımı %100 woka (Ni 78-82% Cr 18-22) 7202 tozu ve ikinci olarak %50 woka 7202 (Ni 78- 82% Cr 18-22) -%50 diamalloy 2002(Ni 66%-Cr 18%) toz karışımı hazırlanarak kaplama yapılmıştır. Kaplama numunelerine mikroyapı incelemesi yapılıp ve sonrasında optik görüntüleri alınmıştır. Kaplanmış numunelerin yüzeyinden içeriye doğru sertlik ölçümleri, XRD analizi, SEM analizi, EDS analizi yapılmış, 2D ve 3D yüzey pürüzlülüğü görüntüleri alınmıştır. Aşınma deneyi alümina bilya kullanılarak farklı hız ve yük parametrelerinde gerçekleştirilmiştir. Aşınma deneyi sonucunda EDS ve SEM analizleri ile aşınma yüzeyleri detaylı bir şekilde incelenmiştir.