AI InsightAs a substitute for cement, silica fume and aggregate 10% of the samples doped YFC 10% of the 28 and 180-day compressive strength, according to the reference sample, respectively, were higher than rates of 17% and 20%
📌 3 Key Takeaways
Abstract
In this study, silica fume (SD), fly ash (FA) and blast furnace slag (HFBS) durability properties of concrete were investigated. Instead of cement SD, HFBS and UK, 5% and 10% percent by weight of single, double and triple mixture of 10% were used. In addition, 5% and 10% percent by weight of aggregate used HFBS. Samples 7, 28, 180-day compressive strength, permeability and wear a 28-day and 60-day sulfate resistance of samples and SEM scans were examined. Strength to strength, and has contributed to the positive contribution of blast furnace slag. As a substitute for cement, silica fume and aggregate 10% of the samples doped YFC 10% of the 28 and 180-day compressive strength, according to the reference sample, respectively, were higher than rates of 17% and 20%
Özet
Bu çalışmada; silis dumanı (SD), uçucu kül (UK) ve yüksek fırın cürufu (YFC) betonların durabilite özellikleri araştırılmıştır. Çimento yerine SD, YFC ve UK, ağırlıkça %5 ve %10 oranlarında tekli, %10 oranında ikili ve üçlü karışım olarak kullanılmıştır. Ayrıca agrega yerine ağırlıkça %5 ve %10 oranlarında YFC kullanılmıştır. Numunelerin 7, 28, 180 günlük basınç dayanımı, 28 günlük numunelerin permeabilite ve aşınma ile 60 günlük sülfat dayanımları ve SEM taramaları incelenmiştir. Yüksek fırın cürufu katkısı dayanıklılığa ve dayanıma olumlu katkı sağlamıştır. Çimento ikamesi olarak %10 oranında silis dumanı ve agrega olarak %10 oranında YFC katkılı numunelerin 28 ve 180 günlük basınç dayanımı, referans numunesine göre sırası ile %17 ve %20 oranlarında daha yüksek bulunmuştur