Abstract
In this study, the mechanical performance of Scotch Pine (Pinus sylvestris L.) and Fir (Abies bornmülleriana Mattf.) wood laminated with different glues were performed and the availability of image analysis method for determining deformations in comparison with the conventional method was investigated. According to the results, the highest bending strength and compression strength parallel to grain in Scotch Pine wood laminated with polyvinyl acetate (PVAc) glue was determined 99.16 N /mm2 and 42.56 N/mm2, respectively. As a result, it is recommended to prefer scotch pine instead of fir in the usage areas in which the high strength properties desired. The deformations data obtained by using the software developed by Labview™ graphical programming compared with conventional method and the results of two methods are consistent with literature.
Özet
Bu çalışmada; farklı tutkallarla lamine edilmiş sarıçam (Pinus sylvestris L.) ve göknar (Abies bornmülleriana Mattf.) odunlarının mekanik performansları belirlenmiş ve görüntü analizi yönteminin deformasyonların belirlenmesinde kullanılabilirliği, klasik yöntemle karşılaştırmalı olarak araştırılmıştır. Çalışma sonuçlarına göre, en yüksek eğilme direnci ve liflere paralel basınç direnci, polivinil asetat (PVAc) tutkalı ile lamine edilen sarıçam odunlarında, sırasıyla 99,16 N/mm2 ve 42,56 N/mm2 olarak belirlenmiştir. Sonuç olarak, yüksek direnç özellikleri istenen kullanım alanlarında göknar yerine sarıçamın tercih edilmesi önerilmektedir. Eğilme testleri sırasında oluşan deformasyonlar, Labview™ grafiksel programlama dili ile geliştirilen yazılım klasik yöntem ile karşılaştırılmış, iki yöntem ile elde edilen veriler literatür ile uyumludur.