Mechanical properties of some aluminum alloys can be changed with precipitation hardening. This intermetallic precipitates are incoherent with the main structure and increased mechanical properties. Cooling rates after solid solution process effects properties after precipitation. In applications, however this is not taken into consideration. In this study, AA 2014 and AA 2024 Aluminium Alloy specimens were hold for one hour at 495$pm$3 °C and formed a solid solution. Specimens were quenched at this temperature with different cooling rtes . later artificial aging was applied at 150 °C and 180 C. The hardness and microstructure variations of the specimens were investigated depending on the cooling rates and artificial aging temperatures.
Özet
Bazı alüminyum alaşımlarına çökelme ısıl işlemi uygulanarak mekanik özellikleri değiştirilebilmektedir. Tek fazlı bölgede uygun bir sıcaklıkta, çözeltiye alma ısıl işlemi ile elde edilen aşırı doymuş katı çözelti, doğal ve/veya yapay olarak yaşlandırılıp iç yapıda çökeltiler oluşturulmaktadır. Bu intermetalik çökeltiler ana yapı ile inkoherent olup malzemenin mekanik özelliklerini arttırmaktadır. Bu işlemin bir parçası olan katı çözeltiye alma işlemi sonrasındaki soğutma koşulları çökelme sonrası özellikleri etkilemektedir. Ancak uygulamada bu durum pek dikkate alınmamaktadır. Bu çalışmada "Aluminum Association "numaralan AA 2014 ve AA 2024 olan alüminyum alaşımları, 495$pm$3 °C'de l saat tutularak katı eriyiğe alınmıştır. Örneklere bu sıcaklıkta farklı soğutma koşullarında su verilmiştir. Daha sonra 150 °C ve 180 °C'de yapay yaşlandırma uygulanmıştır Malzemelerin soğutma koşullarına ve yapay yaşlandırma sıcaklıklarına bağlı olarak sertlik değişimleri ve iç yapılan incelenmiştir.