AI Summary & Key Takeaways
AI InsightResults indicated that PM steel pressed at 750 MPa showed the highest values of yield strength and ultimate tensile strength.
📌 3 Key Takeaways
Abstract
In this work, pressing pressure on microstructure and mechanical properties of non-alloyed powder metallurgy (PM) steels were investigated. The mixed powders prepared in the predetermined proportions were pressed unidirectionally under 650, 700, 750, 800 and 850 MPa. Samples of the tensile experiment were turned into blocks by squeezing with the mould which had been prepared according to ASTM (E 8M) standards of powder metal material tension sample. The pressed samples were sintered at argon atmosphere at 1200ºC for 1 hour. The microstructure of the PM steels was characterised by optic microscope, SEM and EDS. Results indicated that PM steel pressed at 750 MPa showed the highest values of yield strength and ultimate tensile strength. However, when the amount of pressing pressure increased from 750 MPa to 850 MPa, yield strength, ultimate tensile strength and elongation decreased.
Özet
Bu çalışmada, toz metalürjisi (TM) ile üretilen alaşımsız çeliklerde presleme basıncının mikroyapı mekanik özellikleri üzerine etkisi araştırılmıştır. Belirlenen kimyasal kompozisyonda karıştırılan tozlar, ASTM (E 8M) toz metal malzeme standartlarına uygun çekme numunesi şeklindeki kalıpta 650, 700, 750, 800 ve 850 MPa presleme basıncılarında tek yönlü sıkıştırılarak blok haline getirilmiştir. Presleme işlemi gerçekleştirilen numuneler argon atmosferinde 1200°C sinterleme sıcaklığında 1 saat sinterlenmiştir. Üretimi gerçekleştirilen TM çeliklerinin mikroyapısı optik mikroskop, SEM ve EDS ile karakterize edilmiştir. Sonuçlar 750 MPa’da preslenmiş TM çeliklerin en yüksek akma dayanımına ve çekme dayanımına sahip olduğunu göstermiştir. Fakat presleme basıncının 750 MPa’dan 850 MPa’a çıkması ile akma dayanımı ve çekme dayanımı düşmüştür.