The effects of mechanical activation on corrosion resistance of cordierite ceramics

Can Serkan Keskin(SAKARYA ÜNİVERSİTESİ, FEN-EDEBİYAT FAKÜLTESİ)0000-0002-6045-3533
Ceren Ayna Çakır(SAKARYA ÜNİVERSİTESİ, FEN BİLİMLERİ ENSTİTÜSÜ)0009-0000-1224-7228
Hüseyin Altundağ(SAKARYA ÜNİVERSİTESİ, FEN-EDEBİYAT FAKÜLTESİ)0000-0002-3675-4133
Nil Toplan(SAKARYA ÜNİVERSİTESİ, MÜHENDİSLİK FAKÜLTESİ, METALURJİ VE MALZEME MÜHENDİSLİĞİ BÖLÜMÜ, METALURJİ MÜHENDİSLİĞİ PR.)0000-0003-4130-0002
Hüseyin Özkan Toplan(SAKARYA ÜNİVERSİTESİ, MÜHENDİSLİK FAKÜLTESİ, METALURJİ VE MALZEME MÜHENDİSLİĞİ BÖLÜMÜ, METALURJİ MÜHENDİSLİĞİ PR.)0000-0002-3928-2733
Pages
83–88
Publication Date
2023-12-29
🏛️Bibliographic metadata and full text access for this article are provided via DergiPark.
DergiPark Record ↗
✨

AI Summary & Key Takeaways

AI Insight
⚡ TL;DR(Too Long; Didn't Read)

As a result, it has been determined that activated cordierite-based ceramics are more durable, and sulfuric acid solution causes more corrosion than hydrochloric acid.

📌 3 Key Takeaways

🎯
Objective & Hypothesis:The corrosion degrees of produced non-activated and activated cordierite-based ceramics were investigated in hydrochloric and sulfuric acid solutions.
📊
Key Findings & Data:The composition of talc, alumina, and kaolinite powders was mechanically activated in a planetary mill.
💡
Conclusion & Impact:As a result, it has been determined that activated cordierite-based ceramics are more durable, and sulfuric acid solution causes more corrosion than hydrochloric acid.
🔬Design:Araştırma Makalesi
📍Scope:Comprehensive Sample
⚙️Variables:Cordierite · mechanical activation · corrosion resistance

Abstract

The corrosion degrees of produced non-activated and activated cordierite-based ceramics were investigated in hydrochloric and sulfuric acid solutions. The composition of talc, alumina, and kaolinite powders was mechanically activated in a planetary mill. The concentrations of aluminum, magnesium, silicon, calcium, and potassium leached to the acid solutions from non-activated and activated cordierites were measured using ICP-OES. The amorphization of the structures was examined by XRD analysis. As a result, it has been determined that activated cordierite-based ceramics are more durable, and sulfuric acid solution causes more corrosion than hydrochloric acid.

🔖

Cite This Article

Keskin, C. S., Çakır, C. A., Altundağ, H., Toplan, N., Toplan, H. Ö. (2023). The effects of mechanical activation on corrosion resistance of cordierite ceramics. Turkish Journal of Analytical Chemistry, Cilt: 5 Sayı: 2, 83–88. https://doi.org/10.51435/turkjac.1333631

📄 Full Text PDF Viewer

📄

PDF görüntüleyici hazırlanıyor...

References (26)

  1. C. N. Obradovic, N. Dordevic, S. Filipovic, N. Nikolic, D. Kosanovic, M. Mitric, S. Markovic, V. Pavlovic, Influence of mechanochemical activation on the sintering of cordierite ceramics in the presence of Bi2O3 as a functional additive, Powder Technol, 218, 2012, 157–161. https://doi.org/10.1016/j.powtec.2011.12.012.
  2. J. Liao, G. Qing, B. Zhao, Phase equilibria studies in the CaO-MgO-Al2O3-SiO2 system with Al2O3/SiO2 weight ratio of 0.4, Metals, 13(224), 2023, 2-26. https://doi.org/10.3390/met13020224.
  3. W. N. Obradović, V. Pavlović, M. Kachlik, K. Maca, D. Olćan, A. Đorđević, A. Thantshapanyan, B. Vlahović, V. Pavlović, Processing and properties of dense cordierite ceramics obtained through solid-state reaction and pressure-less sintering, Adv Appl Ceram, 118(5), 2019, 241–248. https://doi.org/10.1080/17436753.2018.1548150.
  4. S. Yürüyen, N. Toplan, K. Yıldız, H. Ö. Toplan, The non-isothermal kinetics of cordierite formation in mechanically activated talc–kaolinite–alumina ceramics system, J Therm Anal Calorim, 125(2), 2016, 803–808. https://doi.org/10.1007/s10973-016-5277-1.
  5. C. Başaran, N. Canikoğlu, H. Ö. Toplan, N. Toplan, The crystallization kinetics of the MgO–Al2O3–SiO2–TiO2 glass ceramics system produced from industrial waste, J Therm Anal Calorim, 125(2), 2016, 695–701. https://doi.org/10.1007/s10973-015-5139-2.
  6. A. Peles, N. Đorđevic, N. Obradovic, N. Tadic, V. B. Pavlovic, Influence of prolonged sintering time on density and electrical properties of isothermally sintered cordierite-based ceramics, Sci Sinter, 45(2), 2013, 157-164. https://doi.org/10.2298/SOS1302157P.
  7. Y. Kobayashi, K. Sumi, E. Kato, Preparation of dense cordierite ceramics from magnesium compounds and kaolinite without additives, Ceram Int, 26(7), 2000, 739–43. https://doi.org/10.1016/S0272-8842(00)00013-4.
  8. P. Y. Azimov, S. A. Bushmin, Solubility of minerals of metamorphic and metasomatic rocks in hydrothermal solutions of varying acidity: thermodynamic modeling at 400–800 °C and 1–5 kbar, Geochem. Int+, 45(1), 2007, 1210–1234. https://doi.org/10.1134/S0016702907120038.
  9. A. Harrati, Y. Arkame, A. Manni, A. El Haddar, B. Achiou, A. El Bouari, I. E. A. El Hassani, A. Sdiri, C. Sadik, Cordierite-based refractory ceramics from natural halloysite and peridotite: Insights on technological properties, J Indian Chem Soc, 99(6), 2022, 100496. https://doi.org/10.1016/j.jics.2022.100496.
  10. J. Kang, J. Wang, X. Zhou, J. Yuan, Y. Hou, S. Qian, S. Li, Y. Yue, Effects of alkali metal oxides on crystallization behavior and acid corrosion resistance of cordierite-based glass-ceramics, J Non-Cryst Solids, 481, 2017, 184-190. https://doi.org/10.1016/j.jnoncrysol.2017.10.048.
  11. S. Baitalik, N. Kaya, Processing and properties of cordierite-silica bonded porous SiC ceramics, Ceram Int, 43(17), 2018, 14683–14692. https://doi.org/10.1016/j.ceramint.2017.07.196.
  12. S. Koç¸ N. Toplan, K. Yıldız, H. O. Toplan, Effects of mechanical activation on the non-isothermal kinetics of mullite formation from kaolinite, J Therm Anal Calorim, 103, 2011, 791–796. https://doi.org/10.1007/s10973-010-1154-5.
  13. J. Ding, J. Wang, H. Yang, Z. Liu, C. Yu, X. Li, C. Deng, H. Zhu, Improvement of mechanical properties of composites with surface modified B4C for precision machining, Materials, 16(882), 2023, 2-10. https://doi.org/10.3390/ma16020882.
  14. N. Obradović, S. Filipović, N. Đorđević, D. Kosanović, S. Marković, V. Pavlović, D. Olćan, A. Djordjević, M. Kachlik, K.l Maca, Effects of mechanical activation and two-step sintering on the structure and electrical properties of cordierite-based ceramics, Ceram Int, 42, 2016, 13909–13918. https://doi.org/10.1016/j.ceramint.2016.05.201.
  15. S. K. Nath, S. Kumar, R. Kumar, Effect of mechanical activation on cordierite synthesis through solid-state sintering method, B Mater Sci, 37(6), 2014, 1221–1226. https://doi.org/10.1007/s12034-014-0065-7.
  16. N. G. Đorđević, P. B. Jovanić, Influence of mechanical activation on electrical properties of cordierite ceramics, Sci Sinter, 40, 2008, 47-53. https://doi.org/10.2298/SOS0801047D.
  17. E. Yalamac¸ S. Akkurt, Additive and intensive grinding effects on the synthesis of cordierite, Ceram Int, 32, 2006, 825–832. https://doi.org/10.1016/j.ceramint.2005.06.006.
  18. J. Wu, C. Hu, C. Ping, X. Xu, W. Xiang, Preparation and corrosion resistance of cordierite–spodumene composite ceramics using zircon as a modifying agent, Ceram Int, 44, 2018, 19590–19596. https://doi.org/10.1016/j.ceramint.2018.07.205.
  19. B. Çıtak, D. Kırsever, A. Ayday, H. Boussebha, A. Ş. Demirkıran, The corrosion kinetics of cordierite-based ZrO2 composites obtained from natural zeolite in dilute HCl acid solution, J Compos Mater, 55(20), 2021, 2751–2763. https://doi.org/10.1177/0021998321996751.
  20. P. Balaz, Mechanochemistry In Nanoscience And Minerals Engineering (1. edition), 2008, Germany, Springer.
  21. S. Vyazovkin, Isoconversional Kinetics, Handbook Of Thermal Analysis And Calorimetry, Editors: M.E. Brown, P.K. Gallagher, 2008, Holland, Elsevier.
  22. J. Wu, C. Lu, X. Xu, D. Wang, Y. Zhang, Y. Zhou, Preparation and characterization of cordierite ceramic from coal series kaolin for electronic application, J Aust Ceram Soc, 55, 2019, 943–952. https://doi.org/10.1007/s41779-019-00306-w.
  23. D. Tromans, J. A. Meech, Enhanced dissolution of minerals: microtopography and mechanical activation, Miner Eng, 12(6), 1999, 609–625. https://doi.org/10.1016/S0892-6875(99)00047-3.
  24. D. Tromans, J. A. Meech, Enhanced dissolution of minerals: stored energy, amorphism and mechanical activation, Miner Eng, 14(11), 2001, 1359–1377. https://doi.org/10.1016/S0892-6875(01)00151-0.
  25. E. Elmas, K. Yıldız, N. Toplan, H. Ö. Toplan, Effect of mechanical activation on mullite formation in an alumına-quartz ceramics system, Mater Technol, 47(4), 2013, 413-416. https://doi.org/10.1007/s10973-011-1757-5.
  26. L. Curkovic, M. F. Jelaca, Dissolution of alumina ceramics in HCl aqueous solution, Ceram Int, 35(5), 2009, 2041–2045. https://doi.org/10.1016/j.ceramint.2008.11.007.