AI Summary & Key Takeaways
AI InsightPhysical and mechanical tests, thermal conductivity tests, TGA-DTA and XRD analyzes were performed on the samples and the results were evaluated.
📌 3 Key Takeaways
Abstract
In this study, tincal waste was added to the mortar mixes formed by increasing the cement dosage with pumice light aggregate in different proportions. Acidic pumice aggregate from Nevşehir region of 0-4 mm size was used in the production of concrete mortars. The water / cement ratio of the mixtures was kept constant as 0.50. A total of 6 mixtures were created with three different cement dosages, each with control and tincal waste additives. As a result of various trials, the optimal tincal waste rate was determined as 1%. 10 × 10 × 10 cm cube size samples were produced from each mixture. The samples produced were subjected to 7 and 14 days water curing after being removed from the mold. Physical and mechanical tests, thermal conductivity tests, TGA-DTA and XRD analyzes were performed on the samples and the results were evaluated.
Özet
Bu çalışmada, pomza hafif agregası ile değişik oranlarda çimento dozajı arttırılarak oluşturulan harç karışımlarına tinkal atığı eklenmiştir. Beton harçların üretiminde 0-4 mm boyutundaki Nevşehir yöresi asidik pomza agregası kullanılmıştır. Karışımların su/çimento oranı 0.50 olarak sabit tutulmuştur. Üç farklı çimento dozajında her dozajda kontrol ve tinkal atığı katkılı olmak üzere toplam 6 karışım oluşturulmuştur. Çeşitli denemeler sonucu optimal tinkal atık oranı %1 olarak belirlenmiştir. Her karışımdan 10×10×10 cm küp boyutlu numuneler üretilmiştir. Üretilen numuneler kalıptan alındıktan sonra 7 ve 14 günlük su kürüne tabi tutulmuşlardır. Numuneler üzerinde fiziksel ve mekanik deneyler, termal iletkenlik deneyleri, TGA-DTA ve XRD analizleri yapılarak sonuçlar değerlendirilmiştir.