AI Summary & Key Takeaways
AI InsightFracture types were evaluated using stereomicroscope and SEM.Results: TheraCalPT had statistically significant increased SBS values when compared to other materials(p 0.05).The difference between the adhesive systems and the restorative materials themselves was not significant (p>0.05).Conclusion:The ease of use of TheraCalPT and its strong bonding ability with resin restorative materials may provide support for the idea that it is suitable for pulp interventions.However, since in vitro environmental conditions do not reflect intraoral conditions,it must be supported by clinical studies to understand the actual performance and clinical usability.
📌 3 Key Takeaways
Abstract
Aim:To evaluate shear bond strength(SBS)of three different calcium silicate cements(CSC)with different adhesive systems and restoratives. Materials and methods:NeoMTA2, NeoPutty and TheraCalPT were used as CSC.120 acrylic blocks with a hole in the middle were prepared and divided into three groups(n=40) depending on the CSC used.CSCs were placed in the prepared cavities. Each group was divided into two subgroups and adhesives(Prime&BondNT) and Universal adhesive (Scotchbond)were applied.Then, composite(n=10) and compomer(n=10)were applied and polymerized.The prepared samples were kept at 37oC in a 100% humid environment for 24 hours and shear bond strength test(SBS) was performed with an universal testing device. Fracture types were evaluated using stereomicroscope and SEM.Results: TheraCalPT had statistically significant increased SBS values when compared to other materials(p 0.05).The difference between the adhesive systems and the restorative materials themselves was not significant (p>0.05).Conclusion:The ease of use of TheraCalPT and its strong bonding ability with resin restorative materials may provide support for the idea that it is suitable for pulp interventions.However, since in vitro environmental conditions do not reflect intraoral conditions,it must be supported by clinical studies to understand the actual performance and clinical usability.
Özet
Amaç: Farklı adeziv sistemlerin ve restoratiflerin farklı kalsiyum silikat bazlı simanlara olan makaslama bağlanma kuvvetinin değerlendirilmesidir. Materyal ve metot: NeoMTA2, NeoPutty and TheraCalPT kalsiyum silikat bazlı siman olarak kullanılmıştır. Ortasında delik bulunan 120 akrilik blok hazırlanmış ve 3 gruba (n=40) ayrılmıştır. Kalsiyum silikat simanlar kavitelere yerleştirilmiş, her grup iki alt gruba bölünmüş ve adezivler (Prime &BondNT ve üniversal adeziv (Scotchbond) uygulanmıştır. Her bir gruba kompozit (n=10) ve kompomer (n=10) uygulanmış ve polimerize edilmiştir. Her örnek 37oC’de 100% nemli ortamda 24 saat bekletilmiş ve üniversal test cihazında makaslama bağlanma kuvvetleri ölçülmüştür. Kırılma tipleri SEM ve stereo mikroskopta değerlendirilmiştir. Bulgular: TheraCal PT diğer materyaller ile karşılaştırıldığında istatistiksel olarak yüksek makaslama bağlanma kuvveti göstermiştir(p 0.05). Adeziv sistemler ve restoratif materyaller arasındaki anlamlı bir fark görülmemiştir(p>0.05). Sonuçlar: Theracal PT’nin kullanım kolaylığı ve rezin restoratif materyallere olan yüksek bağlanma kuvveti pulpa tedavilerinde uygun olduğu fikrine destek sağlamaktadır. Bununla birlikte invitro şartlar gerçek ağzı ortamını tam olarak yansıtmayacağı için materyalin gerçek performansı ve klinik kullanılabilirliğini desteklemek için klinik çalışmalara ihtiyaç vardır.