Tensile-shear tests were applied on welded specimens and mechanical performances were determined
📌 3 Key Takeaways
🎯
Objective & Hypothesis:In this study, effect of bakelite interlayer powder on friction stir spot welding of polyethylene materials were investigated. 3 mm thick polyethylene materials were used in the experiments. 900 rpm rotational speed, 70, 100 and 130 seconds stirring time and 60 second waiting time were selected for the welding processes.
📊
Key Findings & Data:In this study, effect of bakelite interlayer powder on friction stir spot welding of polyethylene materials were investigated. 3 mm thick polyethylene materials were used in the experiments. 900 rpm rotational speed, 70, 100 and 130 seconds stirring time and 60 second waiting time were selected for the welding processes.
💡
Conclusion & Impact:Tensile-shear tests were applied on welded specimens and mechanical performances were determined
🔬Design:Makale
📍Scope:Comprehensive Sample
⚙️Variables:Termoplastik polimer · SKNK · kaynak
Abstract
In this study, effect of bakelite interlayer powder on friction stir spot welding of polyethylene materials were investigated. 3 mm thick polyethylene materials were used in the experiments. 900 rpm rotational speed, 70, 100 and 130 seconds stirring time and 60 second waiting time were selected for the welding processes. Tensile-shear tests were applied on welded specimens and mechanical performances were determined
Özet
Bu çalışmada, polietilen malzemelerin sürtünme karıştırma nokta kaynağına bakalit ara tabaka tozunun etkisi araştırılmıştır. Deneylerde 3 mm kalınlığında polietilen malzeme kullanılmıştır. Kaynak işlemlerinde 900 dev/dak dönme devri, 70, 100 ve 130 saniye karıştırma süresi ve 60 saniye takım bekleme süresi deney parametreleri olarak seçilmiştir. Kaynaklı numunelere çekme-makaslama testi uygulanmış ve bağlantı performansları belirlenmiştir
Akkurt, S. (1991). Plastik Malzeme Bilgisi, İstanbul, Birsen Yayınevi.
Karahasanoğu, Erkul, C. M., (1999). Termoplastiklerin Ultrasonik Kaynağı ve Kaynak Parametreleri Plastik Malzemeler ve Teknolojileri Konferansı, İstanbul-Türkiye, 22-34.
Saçak, M., (2012). Polimer Teknolojisi, Ankara, Gazi Kitabevi.
Mert, Ş., Mert, S. (2013). Sürtünme Karıştırma Nokta Kaynak Yönteminin İncelenmesi, İleri
Teknoloji bilimleri Dergisi, Cilt 2, Sayı 1, 26-35.
Kaçar, R., Emre, H.E., Demir, H., Gündüz, S., (2011). Al-Cu-Al Malzeme Çiftinin Sürtünme Karıştırma Nokta Kaynak Kabiliyeti, Gazi Üniv. Mühendislik ve Mimarlık Fakültesi Dergisi, Cilt 26, No 2, 349- 357.
Bilici, M., K., Yukler, A., İ., (2012.). Effects of Welding Parameters on Friction Stir Spot Welding of High Density Polyethylene Sheets, Materials and Design, 33, 545-550.
Bilici, M., K., Yukler, A., İ., (2012). Influence of Tool Geometry and Process Parameters on Macrostructure and Static Strength İn Friction Stir Spot Welded Polyethylene Sheets,
Materials and Design, 33, 145-152.
Kurtulmuş, M., (2012). Friction Stir Spot Welding Parameters for Polypropylene Sheets, Scientific Research and Essays,7(8), 947-956.
Çevik, B. (2013). Polietilen Levhaların Sürtünme Karıştırma Nokta Kaynağı ile Birleşebilirliğine Karıştırıcı Takım Dönme Yönü ve Karıştırma Süresinin Etkisi, İleri
Teknoloji bilimleri Dergisi, Cilt 2, Sayı 3, 28-33.