Study of Vickers´ Micro Hardness on InBi0.85Sb0.15 Single Crystals
- Sayfa
- 231–233
- DOI
- —
Özet
InBi0.85Sb0.15 single crystals have been grown by zone-melting method. The growth velocity was 0.8 cm/h and the freezing interface temperature was 35 °C/cm. A Vickers' projection microscope was used for the study of micro hardness of the crystals. Hardness tests were carried out on the as-cleaved, cold-worked and annealed surfaces of the crystals. The effect of perfection of crystals on micro hardness with respect to the cold-worked, as-cleaved and annealed crystals have been studied and the results are reported.
Abstract
InBi0.85Sb0.15 single crystals have been grown by zone-melting method. The growth velocity was 0.8 cm/h and the freezing interface temperature was 35 °C/cm. A Vickers' projection microscope was used for the study of micro hardness of the crystals. Hardness tests were carried out on the as-cleaved, cold-worked and annealed surfaces of the crystals. The effect of perfection of crystals on micro hardness with respect to the cold-worked, as-cleaved and annealed crystals have been studied and the results are reported.