Production of new type insulation material: Expanded Perlite-Silica aerogel composite

Ömer GÜLER
Öyküm BAŞGÖZ
Çağdaş YAVUZ
Sayfa
95–99
Yayın Tarihi
2021-07-01
DOI
—
🏛️Bu makalenin bibliyografik verileri ve tam metin bağlantısı DergiPark üzerinden sağlanmıştır.
DergiPark Kaydı ↗
✨

Yapay Zeka Hızlı Bakış & Çıkarımlar

AI Insight
⚡ TL;DR(1 Cümlede Hızlı Çıkarım)

The prepared EP-silica aerogel composite was characterized using SEM and BET measurements.

📌 3 Maddede Bu Makale

🎯
Amaç & Hipotez:Silica aerogel is a class of nanoporous material with extremely high porosity (85–99.9 %) and specific surface area (500–1200 m2/g), as in cause very low density, low thermal conductivity.
📊
Temel Bulgular & Veri:To produced EP is heated the perlite to 760–1100 °C, at which point its native water is converted to vapor and the material is caused to expand to 4–20 times its original volume, then the high-porosity and lightweight aggregates are formed.
💡
Sonuç & Katkı:The prepared EP-silica aerogel composite was characterized using SEM and BET measurements.
🔬Tür:Araştırma Makalesi
📍Kapsam:Genişletilmiş Akademik Örneklem
⚙️Değişkenler:Expanded Perlite · Silica aerogel · Insulation building material

Abstract

Silica aerogel is a class of nanoporous material with extremely high porosity (85–99.9 %) and specific surface area (500–1200 m2/g), as in cause very low density, low thermal conductivity. But silica aerogel have some disadvantages. One of this disadvantages is high cost. In this study, to solve this problem has been used low cost precursor which is rice husk ash. Also, we try to improve porosity. To improve the porosity we used expanded perlite (EP). To produced EP is heated the perlite to 760–1100 °C, at which point its native water is converted to vapor and the material is caused to expand to 4–20 times its original volume, then the high-porosity and lightweight aggregates are formed. In this study silica aerogels have been reinforced with EP to product new type composite material which is used as building insulation material. The prepared EP-silica aerogel composite was characterized using SEM and BET measurements.

🔖

Bu Makaleye Atıf Yap

GÜLER, Ö., BAŞGÖZ, Ö., YAVUZ, Ç. (2021). Production of new type insulation material: Expanded Perlite-Silica aerogel composite. Turkish Journal of Engineering, Cilt: 5 - Sayı: 3, 95–99. https://ajindex.com/articles/705072

📄 Tam Metin PDF Okuyucu

📄

PDF görüntüleyici hazırlanıyor...

Kaynakça (1)

  1. ALOthman Z A (2012). A review: Fundamental aspects of silicate mesoporous materials. Materials, 5(12), 2874-2902. DOI: 10.3390/ma5122874 Aravind P R, Shajesh P, Soraru G D & Warrier K G K (2010). Ambient pressure drying: A successful approach for the preparation of silica and silica based mixed oxide aerogels. Journal of Sol-Gel Science and Technology, 54(1), 105-117. DOI: 10.1007/s10971-010-2164-2 Başgöz Ö & Güler Ö (2020). The unusually formation of porous silica nano-stalactite structure by high temperature heat treatment of SiO2 aerogel synthesized from rice hull. Ceramics International, 46(1), 370-380. DOI: 10.1016/j.ceramint.2019.08.271 Feng Q, Chen K, Ma D, Lin H, Liu Z, Qin S & Luo Y (2018). Synthesis of high specific surface area silica aerogel from rice husk ash via ambient pressure drying. Colloids and Surfaces A: Physicochemical and Engineering Aspects, 539, 399-406. DOI: 10.1016/j.colsurfa.2017.12.025 Gregg S J, Sing K S W & Salzberg H W (1967). Adsorption surface area and porosity. Journal of the Electrochemical Society, 114(11), 279C. Kistler S S (1931). Coherent expanded aerogels and jellies. Nature, 127, 741(3211). DOI: 10.1038/127741a0 Kistler S S (1932). Coherent expanded-aerogels. Rubber Chemistry and Technology, 5(4), 600-603. DOI: 10.5254/1.3539386 Li C, Cheng X, Li Z, Pan Y, Huang Y & Gong L (2017). Mechanical, thermal and flammability properties of glass fiber film/silica aerogel composites. Journal of Non-Crystalline Solids, 457, 52-59. DOI: 10.1016/j.jnoncrysol.2016.11.017 Liou T H & Yang C C (2011). Synthesis and surface characteristics of nanosilica produced from alkali-extracted rice husk ash. Materials science and engineering: B, 176(7), 521-529. DOI: 10.1016/j.mseb.2011.01.007 Ma X, Zhou B, Gao W, Qu Y, Wang L, Wang Z, & Zhu Y (2012). A recyclable method for production of pure silica from rice hull ash. Powder Technology, 217, 497-501. DOI: 10.1016/j.powtec.2011.11.009 Nurkowski D, Buerger P, Akroyd J, Mosbach S & Kraft M (2016). Skeletal chemical mechanism of high-temperature TEOS oxidation in hydrogen–oxygen environment. Combustion and Flame, 166, 243-254. DOI: 10.1016/j.combustflame.2016.01.025 Pichór W & Janiec A (2009). Thermal stability of expanded perlite modified by mullite. Ceramics International, 35(1), 527-530. DOI: 10.1016/j.ceramint.2007.10.008 Stolarski M, Walendziewski J, Steininger M & Pniak B (1999). Synthesis and characteristic of silica aerogels. Applied Catalysis A: General, 177(2), 139-148. DOI: 10.1016/S