Dergiler / Tekstil ve Konfeksiyon / 2022 / Cilt: 32 - Sayı: 3

Investigation of the Effect of Raising and Finishing Process on the Physical Performance of 3-Thread Fleece Fabric

Ğassan ASKER
Onur BALCI
Sayfa
183–192
Yayın Tarihi
2022-09-30
DOI
—
🏛️Bu makalenin bibliyografik verileri ve tam metin bağlantısı DergiPark üzerinden sağlanmıştır.
DergiPark Kaydı ↗
✨

Yapay Zeka Hızlı Bakış & Çıkarımlar

AI Insight
⚡ TL;DR(1 Cümlede Hızlı Çıkarım)

As a process, it was determined that the best result was obtained after a single passage with micro silicon pre-softening and raising at a speed of 15m / min, and then a low concentration softening process with a polyvinyl acetate-based binder and softener mixture.

📌 3 Maddede Bu Makale

🎯
Amaç & Hipotez:Within the scope of the study, pre-softening, raising and final softening processes were applied to 2 selected fabrics under different conditions.
📊
Temel Bulgular & Veri:The raising fastness, air permeability and bursting strength tests were performed on the samples obtained after the processes, and the effect of the process conditions on the researched performance values was examined.
💡
Sonuç & Katkı:As a process, it was determined that the best result was obtained after a single passage with micro silicon pre-softening and raising at a speed of 15m / min, and then a low concentration softening process with a polyvinyl acetate-based binder and softener mixture.
🔬Tür:Araştırma Makalesi
📍Kapsam:Genişletilmiş Akademik Örneklem
⚙️Değişkenler:3-thread · fleecy fabric · rasing process

Abstract

Within the scope of the study, pre-softening, raising and final softening processes were applied to 2 selected fabrics under different conditions. The raising fastness, air permeability and bursting strength tests were performed on the samples obtained after the processes, and the effect of the process conditions on the researched performance values was examined. This paper is also detailed by statistical analysis. When the results were examined, it was seen that the best result in terms of raising fastness was the fabric with 50% waste + 50% PES back yarn. As a process, it was determined that the best result was obtained after a single passage with micro silicon pre-softening and raising at a speed of 15m / min, and then a low concentration softening process with a polyvinyl acetate-based binder and softener mixture.

🔖

Bu Makaleye Atıf Yap

ASKER, Ğ., BALCI, O. (2022). Investigation of the Effect of Raising and Finishing Process on the Physical Performance of 3-Thread Fleece Fabric. Tekstil ve Konfeksiyon, Cilt: 32 - Sayı: 3, 183–192. https://ajindex.com/articles/703186

📄 Tam Metin PDF Okuyucu

📄

PDF görüntüleyici hazırlanıyor...

Kaynakça (13)

  1. Marmaralı A.B., (2004). Atkı Örmeciliğine Giriş. Ege Üniversitesi Tekstil ve Konfeksiyon Araştırma-Uygulama Merkezi Yayını, İzmir
  2. Sarker M., Rahman T., Rahman M., (2012). Study on Fleece Knit Fabric. Daffodil International University, Dhaka
  3. Pailthorpe M., (2009). Dry Finishing of Wool Fabrics. The Australian Wool Education Trust Licensee for Educational Activities University of New England
  4. SchindlerW.D, Hauser P. J., (2004). Chemical Finishing of Textile. Woodhead Publishing Ltd. Cambridge, England
  5. Candan C, Önal L., (2002). Dimensional, Pilling, and Abrasion Properties of Weft Knits Made from Open-End and Ring Spun Yarns. Textile Research Journal. 72(2), 164-169
  6. Çoruh E.H., (2004). İnvestigation of Dimensional Stability of Knitted Fabric. (Master’s. Thesis). Textile Engineering University of Gaziantep, Gaziantep
  7. Gülsevin N., (2005). Spor Giysilerin Konfor Özellikleri Üzerine Bir Araştırma. (Yüksek Lisans Tezi). Ege Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Mühendisliği Ana Bilim Dalı, İzmir 8. Meriç B., Demirhan F., (2005). Örme Kumaş ve Giysilerde Yıkama ve Kurutma Sonrası Boyut Değişimlerinin İncelenmesi. Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi, 3, 381-390
  8. Güneşoğlu C., (2006) Spor Giysilik Kumaşların Performans Özelliklerinin Nanoteknolojik Ürünler Kullanılarak Geliştirilmesi ve Aplikasyon Tekniklerinin Araştırılması. (Doktora Tezi). Uludağ Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Mühendisliği Ana Bilim Dalı, Bursa
  9. Erkoç S., (2006). Yuvarlak Örme Makinalarında Üretilen Örme Kumaş Özelliklerini Etkileyen Parametrelerin İncelenmesi. (Yüksek Lisans Tezi). Çukurova Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Mühendisliği Ana Bilim Dalı, Adana
  10. Emirhanova N., Kavuşturan Y., (2008). Effects of Knit Structure on the Dimensional and Physical Properties of Winter Outerwear Knitted Fabrics, Fibres&Textiles in Eastern Europe, (16)2, 69-74
  11. Baçan V., (2010). Endüstriyel Örme Giyim Ürünlerinin Teknolojik Özelliklerinin Belirlenmesi. (Doktora Tezi). Ankara Üniversitesi, Fen Bilimleri Enstitüsü, Ev Ekonomisi (El Sanatları) Ana Bilim Dalı, Ankara
  12. Mezarcıöz S., (2010). Farklı Üretim Teknikleriyle Eğrilmiş İpliklerden Örülen Kumaşların Belirli Özelliklerinin İncelenmesi ve İstatistiksel Modellenmesi. (Doktora Tezi). Çukurova Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Mühendisliği Ana Bilim Dalı, Adana
  13. Özyazgan V., (2010). Çift Plakalı Örgü Kumaşlarda Bitim İşlemlerine Bağlı Boyutsal Değ