THE EFFECT OF HOT WATER AGEING ON THE GLASS FIBER REINFORCED EPOXY COMPOSITE

Gurbet ÖRÇEN
Sayfa
13–24
Yayın Tarihi
2022-10-12
DOI
—
🏛️Bu makalenin bibliyografik verileri ve tam metin bağlantısı DergiPark üzerinden sağlanmıştır.
DergiPark Kaydı ↗
✨

Yapay Zeka Hızlı Bakış & Çıkarımlar

AI Insight
⚡ TL;DR(1 Cümlede Hızlı Çıkarım)

As a result of experimental study, itwas found that the moisture absorption rates increased but the failure loadvalues decreased together with the increase in water temperature andduration of hot water ageing.

📌 3 Maddede Bu Makale

🎯
Amaç & Hipotez:In the present study, the effects of hot water ageing on the glass fiberreinforced epoxy woven composites were experimentally examined.
📊
Temel Bulgular & Veri:Thespecimens in three groups which undamaged, damaged, and single patchrepaired ones were kept in tap water at 50°C and 70°C temperature for 8days and 16 days.
💡
Sonuç & Katkı:As a result of experimental study, itwas found that the moisture absorption rates increased but the failure loadvalues decreased together with the increase in water temperature andduration of hot water ageing.
🔬Tür:Araştırma Makalesi
📍Kapsam:Genişletilmiş Akademik Örneklem
⚙️Değişkenler:Alan Parametreleri

Abstract

In the present study, the effects of hot water ageing on the glass fiberreinforced epoxy woven composites were experimentally examined. Thespecimens in three groups which undamaged, damaged, and single patchrepaired ones were kept in tap water at 50°C and 70°C temperature for 8days and 16 days. At the end of those periods, the moisture absorption rateswere calculated, the maximum failure loads at the end of period of keepingin hot water were determined and the failure modes occurring on thesespecimens were observed and compared. As a result of experimental study, itwas found that the moisture absorption rates increased but the failure loadvalues decreased together with the increase in water temperature andduration of hot water ageing.

🔖

Bu Makaleye Atıf Yap

ÖRÇEN, G. (2022). THE EFFECT OF HOT WATER AGEING ON THE GLASS FIBER REINFORCED EPOXY COMPOSITE. European Journal of Technique, Cilt: 9 - Sayı: 1, 13–24. https://ajindex.com/articles/512056

📄 Tam Metin PDF Okuyucu

📄

PDF görüntüleyici hazırlanıyor...

Kaynakça (13)

  1. Campilho, R.D.S.G., Moura, M.F.S.F., Domingues, J.J.M.S. (2009). Numerical prediction on the tensile residual strength of repaired CFRP under different geometric changes. International Journal of Adhesion & Adhesives, 29, 195– 205
  2. Campilho, R.D.S.G., Mmnoura, M.F.S.F., Domingues, J.J.M.S. (2005). Modelling single and double-lap repairs on composite materials. Composites Science and Technology, 65, 1948–1958
  3. Toudeshky, H. H., Mohammadi, B.(2009).Mixed-mode numerical and experimental fatigue crack growth analyses of thick aluminium panels repaired with composite patches. Composite Structures, 91, 1 –8
  4. Toudeshky, H. H., Mohammadi, B., Daghyani, H. R. (2006). Mixed-mode fracture analysis of aluminium repaired panels using composite patches. Composites Science and Technology, 66, 188–198
  5. Toudeshky, H.H.(2006).Effects of Composite Patches on Fatigue Crack Propagation of Singleside Repaired Aluminum Panels. Composite Structures,76, 243–251
  6. Oudad, W., Bouiadjra, B. B., Belhouari, M., Touzain, S., Feaugas, X. (2009). Analysis of the plastic zone size ahead of repaired cracks with bonded composite patch of metallic aircraft structures. Computational Materials Science, 46, 950–954
  7. Ouinas, D., Bouiadjra, B.B.,Serier, B., Bekkouche, M. S.(2007).Comparison of the effectiveness of boron/epoxy and graphite/epoxy patches for repaired cracks emanating from a semicircular notch edge. Composite Structures, 80, 514–522
  8. Ouinas, D., Sahnoune, M., Bebderdouche, N., Bouiadjdjra, B.B. (2009). Stress İntensity Factor Analysis for Notched Cracked Structure Repaired by Composite Patching. Materials and Design, 30, 2302–2308
  9. Bouiadjra, B. B., Belhouari, M., Serier, B. (2002). Computation of the stress intensity factors for repaired cracks with bonded composite patch in mode I and mixed mode.Composite Structures, 56, 401 –406
  10. Bouiadjra, B.B., Rezgani, L., Ouinas, D., Belhouari, M., Ziadi, A.(2007).Numerical Analysis of the Notch effect and the Behaviour of Notch Crack in Adhesively Bonded Composite Laminates.Computational Materials Science. 38, 759–764
  11. Papanikos, P., Tserpes, K.I., Pantelakis, Sp.(2007). Initiation and progression of composite patch debonding in adhesively repaired cracked metallic sheets.Composite Structures,81,303–311
  12. Umamaheswar, T.V.R.S.(1999).Singh, R., Modelling of a patch repair to a thin cracked sheet. Engineering Fracture Mechanics, 62, 267-289
  13. Charalambides, M.N., Hardouin, R., Kinloch, A