AI InsightAccording to the results, the mechanochemistrycontributed positively to the dissolution of manganese due to the increased leachability oflaterite at low temperature and in a short time with low acid consumption.
📌 3 Maddede Bu Makale
Abstract
This study investigates the effect of the process involving a combination of sodium-basedreagent-assisted mechanochemical conversion (NaOH-MC) and leaching, which wasdeveloped to provide highly efficient nickel recovery, on the amount of dissolved manganeseduring nickel recovery. For this purpose, firstly laterite was treated with NaOH as a reagentand then leaching performed in sulphuric acid medium. Response Surface Methodology(RSM) was successfully used as a statistical approach to determine the effect of parametersfor both processes and to optimize processes conditions in terms of dissolved manganese. Inoptimum conditions determined as 0.5 M H2SO4, 55 mL/g liquid to solid ratio, 75 ºC and 30min; dissolution amount of manganese from NaOH-MC treated laterite was achieved as97.54% ± 1.06 (N = 2) with standard deviation. In addition, the dissolution behavior ofmanganese was defined by a control mechanism, a combination of chemical reaction anddiffusion based on the shrinking core kinetic model. The activation energy of manganesedissolution was found as 35.42 kJ/mol. According to the results, the mechanochemistrycontributed positively to the dissolution of manganese due to the increased leachability oflaterite at low temperature and in a short time with low acid consumption.