Investigation of joining properties of AA 5083 material in MIG and TIG weldings

Hatice VAROL ÖZKAVAK
Serdar MERCAN
Sayfa
951–964
Yayın Tarihi
2022-10-12
DOI
—
🏛️Bu makalenin bibliyografik verileri ve tam metin bağlantısı DergiPark üzerinden sağlanmıştır.
DergiPark Kaydı ↗
✨

Yapay Zeka Hızlı Bakış & Çıkarımlar

AI Insight
⚡ TL;DR(1 Cümlede Hızlı Çıkarım)

As a result, it was found that samples joined by MIG welding have higher strength and ductility, along with a lower amount of microstructural defects compared to their counterparts joined by TIG welding.

📌 3 Maddede Bu Makale

🎯
Amaç & Hipotez:AA 5083 Aluminum alloys begin to be replaced steels in automobiles, ships, and high-speed trains by providing reduced energy consumption and low carbon emissions thanks to their low densities, good weldabilities, and high corrosion resistance.
📊
Temel Bulgular & Veri:During the production of high speed trains, which are of special importance for our country, the proper selection of joining method for AA5083 increases the production speed.
💡
Sonuç & Katkı:As a result, it was found that samples joined by MIG welding have higher strength and ductility, along with a lower amount of microstructural defects compared to their counterparts joined by TIG welding.
🔬Tür:Araştırma Makalesi
📍Kapsam:Genişletilmiş Akademik Örneklem
⚙️Değişkenler:Alan Parametreleri

Abstract

AA 5083 Aluminum alloys begin to be replaced steels in automobiles, ships, and high-speed trains by providing reduced energy consumption and low carbon emissions thanks to their low densities, good weldabilities, and high corrosion resistance. During the production of high speed trains, which are of special importance for our country, the proper selection of joining method for AA5083 increases the production speed. In this study, AA5083 alloys with 8 mm thickness were butt-welded under different parameters by using MIG and TIG weldings. It was aimed to determine the changes in microstructure and mechanical properties of welded samples, and also to specify the proper welding method. As a result, it was found that samples joined by MIG welding have higher strength and ductility, along with a lower amount of microstructural defects compared to their counterparts joined by TIG welding.

🔖

Bu Makaleye Atıf Yap

ÖZKAVAK, H. V., MERCAN, S. (2022). Investigation of joining properties of AA 5083 material in MIG and TIG weldings. Cumhuriyet Science Journal, Cilt: 42 - Sayı: 4, 951–964. https://ajindex.com/articles/477582

📄 Tam Metin PDF Okuyucu

📄

PDF görüntüleyici hazırlanıyor...

Kaynakça (13)

  1. Mercan E., Ayan Y., Kahraman N., Investigation on joint properties of AA5754 and AA6013 dissimilar aluminum alloys welded using automatic GMAW, Engineering Science and Technology, an International Journal, 23 (2020) 723-731
  2. Franz D., Szilvasi T., Irran E., Inoue S., A monotopic aluminum telluride with an Al= Te double bond stabilized by N-heterocyclic carbenes, Nature Communication, 6 (2015) 1-6
  3. Zamzami I.A., Susmel L., Nominal and local stress quantities to design aluminium-to-steel thin welded joints against fatigue, International Journal of Fatigue, 101 (2) (2017) 137–158
  4. Heinen P., Wu H., Olowinsky A., GillnerA., Helium-tight laser beam welding of aluminum with brillant laser beam radiation, Physics Procedia, 56 (2014) 554–565
  5. Li J., Xue J., Zhang Z., Hu Y., Effects of thermal frequency on microstructures, Applied Science, 8 (4) (2018) 540
  6. Borrego L.P., J.D. Costa, J.S., Jesus, A.R. Loureiro, J.M. Ferreira., Fatigue life improvement by friction stir processing of 5083 aluminium alloy MIG butt welds, Theoretical and Applied Fracture Mechanics,70 (2014)68-74
  7. Ilman M.N., Triwibowo N.A., Wahyudianto A., Muslih M.R., Environmentally assisted fatigue behaviour of stress relieved metal inert gas (MIG) AA5083 welds in 3.5% NaCl solution, International Journal of Fatigue, 100 (2017) 285– 295
  8. Perel V.Y., Misak H.E, Mall S., Jain V.K, Biaxial fatigue crack growth behavior in aluminium alloy 5083-H116 under ambient laboratory and saltwater environments, Journal of Material Engineering Performance, 24(4) (2015) 1565–72
  9. Abkenar M.R., Kihl D.P., Manzari M.T., Fatigue tests on aluminium specimens subjected to constant and random amplitude loadings, ASME Journal of Materials Technology, 138(2016) 1–7
  10. Holtz R.L., Pao P.S., Bayles R.A., Longazel T.M., Goswami R., Corrosion fatigue of aluminium alloy 5083-H131 sensitizes at 448 K (175°C), Metal Materials Transaction A, 43 A (2012) 2839–2849
  11. Miller K.W., Chao Y.J., Wang P.C., Performance Comparison of Spot-Welded, Adhesive Bonded, and Self-Piercing Riveted Aluminium Joints, ASM proceedings of the international conference: trends in welding research, (1998) 910–915
  12. Costa J.D.M, Jesus J.S., Loureiro A., Ferreira J.A.M., Borrego L.P., Fatigue life improvement of mig welded aluminum T-joints by friction stir processing, Internatinal Journal of Fatigue, 61 (2014) 244–54
  13. Messler Jr R.W., Principles of welding: processes, physics, chemistry and metallurgy, 1st ed