The limited study on high temperature sintering using SiC and B4C showed gradual improvements in strength sintering above 750 ?C, which can be attributed to the in-situ formation of Si as well as SiB, where n= 2, 4, 6 .... n.
📌 3 Maddede Bu Makale
🎯
Amaç & Hipotez:Considering the demands for the high strength and corrosion resistant powder metallurgy parts, the most direct yet cost effective method of production of borides can be possibly be routed through the in-situ solid-state reaction in powder metallurgy.
📊
Temel Bulgular & Veri:Going by the known reaction paths, a composition of boron carbide and silicon carbide in combination with aluminum was investigated at three different sintering temperatures in order to see the effect of boron carbide on mechanical properties of aluminum under conventional high temperature sintering conditions.
💡
Sonuç & Katkı:The limited study on high temperature sintering using SiC and B4C showed gradual improvements in strength sintering above 750 ?C, which can be attributed to the in-situ formation of Si as well as SiB, where n= 2, 4, 6 .... n.
🔬Tür:Araştırma Makalesi
📍Kapsam:Genişletilmiş Akademik Örneklem
⚙️Değişkenler:Alan Parametreleri
Abstract
Considering the demands for the high strength and corrosion resistant powder metallurgy parts, the most direct yet cost effective method of production of borides can be possibly be routed through the in-situ solid-state reaction in powder metallurgy. Going by the known reaction paths, a composition of boron carbide and silicon carbide in combination with aluminum was investigated at three different sintering temperatures in order to see the effect of boron carbide on mechanical properties of aluminum under conventional high temperature sintering conditions. The limited study on high temperature sintering using SiC and B4C showed gradual improvements in strength sintering above 750 ?C, which can be attributed to the in-situ formation of Si as well as SiB, where n= 2, 4, 6 .... n.
🔖
Bu Makaleye Atıf Yap
ŞİMŞEK, T., BARIŞ, M., CHATTOPADHYAY, A. K., BİLEN, M. (2022). In-situ formation of borides and enhancement of powder metallurgy properties. Bor Dergisi, Cilt: 2 - Sayı: 2, 97–101. https://ajindex.com/articles/467485
Chattopadhyay A. K., Selective migration of metals and metal borides to strengthen boron carbide, Met. Powder Rep., 71(2), 106, 2016
Chattopadhyay A. K., Yilmaz O., Bilen M., Baris M., Strengthening boron carbide and prevention of high pressure amorphization by inducing metals or metal borides across the grain boundary during hot pressing or sintering, Adv. Powder. Metall. Part. Mater., 7, 1-12, 2015
Viala J.C., Bouix J., Gonzalez G, Esnouf C, Chemical reactivity of aluminium with boron carbide, J. Mater Sci., 32, 4559-4573, 1997
Oh S.Y., Cornie J.A., Russel K.C., Wetting of ceramic particulates with liquid aluminum alloys: Part II. Study of wettability, Metall. Trans. A, 20, 533-541, 1989
Nobel B., Trousdale A.J., Haris S.J., J. Mater Sci., 32, 5969, 1997
Gokmese H., Bostan, B., Baris, M., Fabrication and characterization of nanoceramic particle al2o3/b4 c compositeby mechanochemical approach, Inorganic and Nano-Metal Chemistry, 47 (3), 416-422, 2017
German R. M., Powder metallurgy and particulate materials processing, MPIF, 377-78, 2005
MPIF Standard: Method for determination of transverse rupture strength of powder metallurgy materials, MPIF Standard Test Methods, 2006.