IMPORTANCE OF POLYMER SIZE RHEOLOGY FOR EFFICIENT SIZING OF COTTON WARP YARNS

Suzana DJORDJEVIC
Ljubisa NIKOLIC
Snezana UROSEVIC
Dragan DJORDJEVIC
Sayfa
77–82
Yayın Tarihi
2012-06-29
DOI
—
🏛️Bu makalenin bibliyografik verileri ve tam metin bağlantısı DergiPark üzerinden sağlanmıştır.
DergiPark Kaydı ↗
✨

Yapay Zeka Hızlı Bakış & Çıkarımlar

AI Insight
⚡ TL;DR(1 Cümlede Hızlı Çıkarım)

Based upon the results on polymer size features as well as on certain physical parameters of sized yarn, some rheology and kinetic parameters cause appropriate behaviour of polymer molecules in solution, which improves bonding and penetration ability into yarn, and then it directly influences on more efficient warp sizing.

📌 3 Maddede Bu Makale

🎯
Amaç & Hipotez:This paper is about rheology of copolymer acryl amide and acrylic acid solution, as potential agent for warp sizing of cotton yarn as well as in the warp sizing process.
📊
Temel Bulgular & Veri:Based on the results, it was determined that decrease of polymer size concentration conditions viscosity decrease.
💡
Sonuç & Katkı:Based upon the results on polymer size features as well as on certain physical parameters of sized yarn, some rheology and kinetic parameters cause appropriate behaviour of polymer molecules in solution, which improves bonding and penetration ability into yarn, and then it directly influences on more efficient warp sizing.
🔬Tür:Araştırma Makalesi
📍Kapsam:Genişletilmiş Akademik Örneklem
⚙️Değişkenler:Polymer size · Rheology · Sizing

Abstract

This paper is about rheology of copolymer acryl amide and acrylic acid solution, as potential agent for warp sizing of cotton yarn as well as in the warp sizing process. The changes of rheology parameters of polymer size are analyzed depending upon concentration and temperature. Based on the results, it was determined that decrease of polymer size concentration conditions viscosity decrease. The temperature increase causes decrease of polymer solution viscosity for the same concentration. In addition, kinetic parameters at various temperatures were monitored, where i.e. activation energy of polymer size decreases with the decrease of its concentration. Higher polymer size concentration enables more deposit on the yarn. Based upon the results on polymer size features as well as on certain physical parameters of sized yarn, some rheology and kinetic parameters cause appropriate behaviour of polymer molecules in solution, which improves bonding and penetration ability into yarn, and then it directly influences on more efficient warp sizing.

🔖

Bu Makaleye Atıf Yap

DJORDJEVIC, S., NIKOLIC, L., UROSEVIC, S., DJORDJEVIC, D. (2012). IMPORTANCE OF POLYMER SIZE RHEOLOGY FOR EFFICIENT SIZING OF COTTON WARP YARNS. Tekstil ve Konfeksiyon, Cilt: 22 - Sayı: 2, 77–82. https://ajindex.com/articles/46283

📄 Tam Metin PDF Okuyucu

📄

PDF görüntüleyici hazırlanıyor...

Kaynakça (14)

  1. Mostafa, Kh.M., and El-Sanaba, A.A., 1997, "Carboxyl-containing starch and hydrolyzed starch derivatives as size base materials for cotton textiles", Polymer Degradation and Stability, 55, 181-184
  2. Hebeish, A., Abdel-Rahman, A., El-Hilw, Z., and Hashem, M., 2005, "Cationized Starch Derived From Pre-Oxidized Starch For Textile Sizing and Printing", Starch/Stärke, 57, 616-623
  3. Abdel-Mohdy, F.A., 1998, "Improving the sizeability of some sizing materials based on starch composites", Pigment & Resin Technology, 27, 180-186
  4. Moreau, J.P., 1986, "Evaluation of Fabrics Woven with Durable Polymeric Sizing Agents", Textile Research Journal, 56, 627-634
  5. Rogovina, L.Z., Vasil'ev, V.G., Churochkina, N.A., and Pryakhina, T.A., 2003, "Rheology of Hydrophobically Modified Polymers", Journal of Engineering Physics and Thermophysics, 76, 527-534
  6. Litaeim, Y., and Dhahbi, M., 2010, "Measurements and correlation of viscosity and conductivity for the mixtures of ethylammonium nitrate with organic solvents", Journal of Molecular Liquids, 155, 42-50
  7. Cassagnau, P., Montfort, J.P., Marin, G., and Monge, P., 1993, "Rheology of polydisperse polymers: relationship between intermolecular interactions and molecular weight distribution", Rheologica Acta, 32, 156-167
  8. Moreau, J.P., 1984, "Research on Polymers as Sizing Agents-Laboratory to Loom", Journal of Industrial Textiles, 13, 258-269
  9. Slauson, S.D., Miller, B., and Rebenfeld, L., 1984, "Physicochemical Properties of Sized Yams: Part I: Initial Studies", Textile Research Journal, 54, 655664
  10. Zhu, Z., Qiao, Z., Kang, C., and Li, Y., 2004, "Effect of acrylate constituent units on the adhesion of polyacrylate sizes to fiber substrates", Journal of Applied Polymer Science, 91, 3016-3022
  11. Truonga, N.D., Galina, J.C., Françoisa, J., and Pham, Q.T., 1986, "Microstructure of acrylamide-acrylic acid copolymers: 2. As obtained by direct copolymerization", Polymer, 7, 467-475
  12. François, J., Truong, N.D., Medjahdi, G., and Mestdagh, M.M., 1997, "Aqueous solutions of acrylamide-acrylic acid copolymers: stability in the presence of alkalinoearth cations", Polymer, 38, 6115-6127
  13. Zhu, Z., Jin, and E., Yang, Y., 2009, "Incorporation of aliphatic units into aromatic water-soluble polyesters to improve the performances for warp sizing", Fibers and Polymers, 10, 583-589
  14. Slauson, S.D., Miller, B., and Rebenfeld, L., 1985, "Physicochemical Properties of Sized Yams: Part II: Two-Component Sizing Systems",