INVESTIGATION OF MECHANICAL AND METALLOGRAPHIC PROPERTIES OF TWO DIFFERENT ALUMINUM ALLOYS JOINED WITH FRICTION STIR WELDING METHOD USING DIFFERENT WELDING PARAMETERS
The hardness values measured in weld areas were higher in the EN AW-6082 base metal side compared with EN AW-5083 base metal side.
📌 3 Maddede Bu Makale
🎯
Amaç & Hipotez:In this study two aluminum alloy materials of EN AW-5083-H111 and EN AW-6082-T651 were joined with Friction Stir Welding considering the parameters as the tool shoulder diameter, spindle speed and feed rate.
📊
Temel Bulgular & Veri:The mechanical properties of the weld joints such as yield strength, tensile strength and micro-hardness and metallographic properties were investigated comparatively with the use of these welding parameters.
💡
Sonuç & Katkı:The hardness values measured in weld areas were higher in the EN AW-6082 base metal side compared with EN AW-5083 base metal side.
In this study two aluminum alloy materials of EN AW-5083-H111 and EN AW-6082-T651 were joined with Friction Stir Welding considering the parameters as the tool shoulder diameter, spindle speed and feed rate. The mechanical properties of the weld joints such as yield strength, tensile strength and micro-hardness and metallographic properties were investigated comparatively with the use of these welding parameters. The yield strength of the weld joints were determined to be between 136-217 MPa while the tensile strengths were between 159-230 MPa and the percent elongations were between 2.28-5.44 %. The hardness values measured in weld areas were higher in the EN AW-6082 base metal side compared with EN AW-5083 base metal side.
ÖCALIR, Ş., EŞME, U., BOĞA, C., KÜLEKCİ, M. K. (2021). INVESTIGATION OF MECHANICAL AND METALLOGRAPHIC PROPERTIES OF TWO DIFFERENT ALUMINUM ALLOYS JOINED WITH FRICTION STIR WELDING METHOD USING DIFFERENT WELDING PARAMETERS. Sigma Mühendislik ve Fen Bilimleri Dergisi, Cilt: 38 - Sayı: 3, 1333–1349. https://ajindex.com/articles/419075
Kulekci, M., K., Şik A., Kaluç, E. (2008). Effects of tool rotation and pin diameter on fatigue properties of friction stir welded lap joints, International Journal of Advanced Manufacturing Technology, Vol. 36, 877-882, doi: 10.1007/s00170-006-0901-z
Kaynak Tekniği El Kitabı-Yöntemler Ve Donanımlar, Anık, S. (1991), from http://www.gedikegitimvakfi.org.tr/wp- content/uploads/2013/12/library_6.pdf, accessed September 15, 2019
Hou, K., Baeslack, W. (1996). Characterization of the heat-affected zone in gas tungsten arc welded aluminium alloy 2195-T8, Journal of Materials Science Letters, Vol. 15, No. 3, 239–244, doi:10.1007/BF00274462
Koteswara Rao, S.R., Madhusudhan Reddy, G., Srinivasa Rao, K., Kamaraj, M., Prasad Rao, K. (2005). Reasons for superior mechanical and corrosion properties of 2219 aluminum alloy electron beam welds, Materials Characterization, Vol. 55, No. 4-5, 345–354, doi: 10.1016/j.matchar.2005.07.006
Paston, M., Zhao, H., Martukannitz, R.P., Debroy, T. (1999). Porosity, underfill and magnesium loss during continuous wave Nd: YAG laser welding of thin plates of aluminium alloy 5182 and 5754, Materials Science, 207–216
Yeniyil, E., Boga, C., Esme, U. (2019). Effects of ultrasonic welding parameters for solar collector applications, Materials Testing, Vol. 61, No. 4, 344-348,
Klobcar, D., Kosec, L., Pietras, A., Smolej, A. (2012). Friction-stir welding of aluminium alloy 5083, Materials and Technology, Vol. 46, No. 5, 483–488