The ferromagnetic order in the $Cu_{1-x}Co_x$ films was between 2.5-29%.
📌 3 Maddede Bu Makale
🎯
Amaç & Hipotez:The magnetic properties of $Cu_{1-x}Co_x$ alloy films prepared by electrodeposition technique were investigated by Alternating Gradient Force Magnetometer.
📊
Temel Bulgular & Veri:The magnetization curves of $Cu_{0.94}Co_{0.06}$, $Cu_{0.87}Co_{0.13}$ and $Cu_{0.74}Co_{0.26}$ films were easily saturated while the other $Cu{1 - x}Co_x$ samples with x= 0.17, 0.19 and 0.21 had more inclined magnetization curves.
💡
Sonuç & Katkı:The ferromagnetic order in the $Cu_{1-x}Co_x$ films was between 2.5-29%.
🔬Tür:Araştırma Makalesi
📍Kapsam:Genişletilmiş Akademik Örneklem
⚙️Değişkenler:Alan Parametreleri
Özet
The magnetic properties of $Cu_{1-x}Co_x$ alloy films prepared by electrodeposition technique were investigated by Alternating Gradient Force Magnetometer. The magnetization curves of $Cu_{0.94}Co_{0.06}$, $Cu_{0.87}Co_{0.13}$ and $Cu_{0.74}Co_{0.26}$ films were easily saturated while the other $Cu{1 - x}Co_x$ samples with x= 0.17, 0.19 and 0.21 had more inclined magnetization curves. The saturation magnetization value of$Cu_{1-x}Co_x$ film increased with increasing Co content in the film. The minimum values of the ratio of remanence to magnetization and the coercive field were determined in the $Cu_0.81Co_0.19$ alloy film among the others. The ferromagnetic order in the $Cu_{1-x}Co_x$ films was between 2.5-29%.
🔖
Bu Makaleye Atıf Yap
BAKKALOĞLU, Ö. F., KARAHAN, İ. H., EFEOĞLU, H., YILDIRIM, M., ÇEVİK, U., YOĞURTÇU, Y. K. (2001). Magnetization measurements on electrodeposited $Cu_{1-x}Co_x$ alloy films. Turkish Journal of Physics, Cilt: 25 - Sayı: 5, 451–454. https://ajindex.com/articles/378655
S.S.P. Parkin, Z.G. Li and D.J. Smith, Appl. Phys. Lett. 58 (1991) 2710
A.J.R. Ives, R.J. Hicken, J.A.C. Bland, C. Daboo, M. Gester and S.J. Gray, J. Appl. Phys.75 (1994) 6458
C. Dupas, E. Kolb, K. Ledang, J.P. Renard, P. Veillet, E. Velu and D. Renard, J. Magn.Mag. Mater. 128 (1993) 361
P. Nallet, E. Chassaing, M.G. Walls and M.J. Hytch, J. Appl. Phys. 79 (1996) 6884.vA.E.Berkowitz, J.R. Mitchell, M.J. Carey, A.P. Young, S. Zhang, F.E. Spada, F.T. Parker,A. Hutten and G. Thomas, Phys Rev. Lett. 68 (1992) 3745
H.J. Blythe and V.M. Fedosyuk, J. Magn. Mag. Mater. 155 (1996) 352.