The results indicate that at different rates of solidification undercooling, diffusion and convection mechanisms affect the microsegregation of nickel and copper in the cast materials to various extents.
📌 3 Maddede Bu Makale
🎯
Amaç & Hipotez:The distribution of nickel in dendrite arms and in interdendritic regions of copper-10% nickel alloy solidified under production conditions designed to provide 4 different cooling rates was investigated.
📊
Temel Bulgular & Veri:The distribution of nickel in dendrite arms and in interdendritic regions of copper-10% nickel alloy solidified under production conditions designed to provide 4 different cooling rates was investigated.
💡
Sonuç & Katkı:The results indicate that at different rates of solidification undercooling, diffusion and convection mechanisms affect the microsegregation of nickel and copper in the cast materials to various extents.
The distribution of nickel in dendrite arms and in interdendritic regions of copper-10% nickel alloy solidified under production conditions designed to provide 4 different cooling rates was investigated. The results indicate that at different rates of solidification undercooling, diffusion and convection mechanisms affect the microsegregation of nickel and copper in the cast materials to various extents.
Abstract
The distribution of nickel in dendrite arms and in interdendritic regions of copper-10% nickel alloy solidified under production conditions designed to provide 4 different cooling rates was investigated. The results indicate that at different rates of solidification undercooling, diffusion and convection mechanisms affect the microsegregation of nickel and copper in the cast materials to various extents.
DÜNDAR, S. (2004). Dendritic Solidification in a Copper Nickel Alloy. Turkish Journal of Engineering and Environmental Sciences, Cilt: 28 - Sayı: 2, 129–134. https://ajindex.com/articles/369205