As a result of the study, it was determined that geopolymers prepared with GGBFS can also be used in the areas where blast furnace slag cement would be used.
📌 3 Maddede Bu Makale
🎯
Amaç & Hipotez:Geopolymers are obtained by various methods in different alkaline environments by changing compositions and crystal structures of pozzolans, which have Al and Si oxide compounds in their structures and carry little or no hydraulic characteristics.
📊
Temel Bulgular & Veri:In this study, mechanical and physical characteristics of geopolymer mortars manufactured with ground granulated blast furnace slag (GGBFS) and activated with sodium silicate (water glass) were determined and also their SEM-EDS analyses were performed.
💡
Sonuç & Katkı:As a result of the study, it was determined that geopolymers prepared with GGBFS can also be used in the areas where blast furnace slag cement would be used.
Geopolymers are obtained by various methods in different alkaline environments by changing compositions and crystal structures of pozzolans, which have Al and Si oxide compounds in their structures and carry little or no hydraulic characteristics. In this study, mechanical and physical characteristics of geopolymer mortars manufactured with ground granulated blast furnace slag (GGBFS) and activated with sodium silicate (water glass) were determined and also their SEM-EDS analyses were performed. As a result of the study, it was determined that geopolymers prepared with GGBFS can also be used in the areas where blast furnace slag cement would be used.
ÇOMAK, B. (2018). Engineering Characteristics of Geopolymer Mortars Manufactured with Ground Granulated Blast Furnace Slag. Süleyman Demirel Üniversitesi Fen Bilimleri Enstitüsü Dergisi, Cilt: 22 - Sayı: 2, 470–476. https://ajindex.com/articles/310150
Aleem, M. I. A., Arumairaj, P. D. 2012. Geopolymer Concrete-A Revıew. International Journal of Engineering Sciences & Emerging Technologies. 1(2), 118-22
Köleli, Y. 2015. TR63 Bölgesi Çimento Sektör Raporu. Doğu Akdeniz Kalkınma Ajansı: Doğu Akdeniz Kalkınma Ajansı
Tokyay, M., Erdoğdu, K. 2009. Cüruflar ve Cüruflu Çimentolar. TÇMB / AR-GE / Y 972. Ankara: TÇMB
Baradan, B., Yazıcı, H., Aydın, S. 2012. Beton. İzmir: Dokuz Eylül Üniversitesi Mühendislik Fakültesi Yayınları
Dorum, A., Koçak, Y., Yılmaz, B., Uçar, A. 2009. The Effects of Blast Furnace Slag on the Cement Surface Properties and Hydration. Journal of the Institute of Science and Technology of Dumlupinar University. 19, 47-58
El-Didamony, H., Amer, A. A., El-Sokkary, T. M., Abd-El-Aziz, H. 2013. Effect of substitution of granulated slag by air-cooled slag on the properties of alkali activated slag. Ceramics International. 39(1), 171-81
Praveen, J. A., Senthilkumar, P., Sridhar, J., Nickson, S. 2015. A Comparative Study of Alkali Activated Slag and Fly Ash-Based Geopolymer Concrete. International Journal of Innovative Research in Science, Engineering and Technology. 2001, 10151-10156
Universit, B., Benbouali, H. 2009. Some Parameters Affecting the Heat of Hydration of Blast-Furnace Slag. SBEIDCO – 1st International Conference on Sustainable Built Environment Infrastructures in Developing Countries ENSET. (Durability of materials and structures), 8-16
Davidovits, J. 1991. Geopolymers: Inorganic Polymeric New Materials. Journal of Thermal Analysis. 37, 1633-1656
Xu, H., Van Deventer, J. S. J. 2000. The geopolymerisation of alumino-silicate minerals. International Journal of Mineral Processing. 59(3), 247-266
Görhan, G., Kürklü, G. 2014. Alkali Tuz İçeriğinin Geopolimer Cephe Kaplama Malzemesi Özelliklerine Etkisi. 7 Ulusal Çatı & Cephe Sempozyumu. İstanbul, 51-58
Altan, E., Erdogan, S. T. 2012. Alkali activation of a slag at ambient and elevated temperatures. Cement Concrete Comp., 34(2), 131-139
Chi, M. 2012. Effects of dosage of alkali-activated solution and curing conditions on the properties and durability of alkali-activated slag concrete. Construction and Building Materials. 35, 240-245
Dutta, D., Ghosh, S. 2014. Durability Study of Geopolymer Paste Blended with Blast Furnace Slag. IOSR Journal of Mechanical and Civil Engineering, 11(2), 73-79
Madheswaran, C. K., Gnanasundar, G, Gopalakrishnan, N. 2013. Effect of mol