Characterization of W2B Nanocrystals Synthesized by Mechanochemical Method

Mustafa Barış
Tuncay Şimşek
Hakan GÖKMEŞE
Adnan AKKURT
Sayfa
45–51
Yayın Tarihi
2016-03-24
DOI
—
🏛️Bu makalenin bibliyografik verileri ve tam metin bağlantısı DergiPark üzerinden sağlanmıştır.
DergiPark Kaydı ↗
✨

Yapay Zeka Hızlı Bakış & Çıkarımlar

AI Insight
⚡ TL;DR(1 Cümlede Hızlı Çıkarım)

Crystallite size and specific surface area of the W2B nanocrystals were determined as 13.61 nm and 18 m2/g respectively.

📌 3 Maddede Bu Makale

🎯
Amaç & Hipotez:In this study; W2B nanocrystals were synthesized with B2O3/Mg/WO3 starting materials via mechanochemical method.
📊
Temel Bulgular & Veri:Results showed that W2B nanocrystals were obtained successfully without different tungsten compounds after 30 h milling and purification in 2 M HCl solution.
💡
Sonuç & Katkı:Crystallite size and specific surface area of the W2B nanocrystals were determined as 13.61 nm and 18 m2/g respectively.
🔬Tür:Araştırma Makalesi
📍Kapsam:Genişletilmiş Akademik Örneklem
⚙️Değişkenler:Ball milling · mechanochemical synthesis · nanocrystals

Abstract

In this study; W2B nanocrystals were synthesized with B2O3/Mg/WO3 starting materials via mechanochemical method. Starting materials were mixed according to the reaction stoichiometry and reduction processes were performed in a planetary ball mill under Argon gas atmosphere. Phase and morphology structure of particles were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy with energy-dispersive X-ray spectroscopy (TEM/EDX) and the specific surface area was measured by Brunauer-Emmet-Teller (BET) theory. The effect of milling period and molar ratios of starting powders were investigated in detail. Results showed that W2B nanocrystals were obtained successfully without different tungsten compounds after 30 h milling and purification in 2 M HCl solution. Coaxial/spherical shaped and agglomerated W2B nanocrystals were observed by microstructural examinations. Crystallite size and specific surface area of the W2B nanocrystals were determined as 13.61 nm and 18 m2/g respectively.

🔖

Bu Makaleye Atıf Yap

Barış, M., Şimşek, T., GÖKMEŞE, H., AKKURT, A. (2016). Characterization of W2B Nanocrystals Synthesized by Mechanochemical Method. Bor Dergisi, Cilt: 1 - Sayı: 1, 45–51. https://ajindex.com/articles/252168

📄 Tam Metin PDF Okuyucu

📄

PDF görüntüleyici hazırlanıyor...

Kaynakça (16)

  1. Li Q., Zhou D., Zheng W., Ma Y., Chen C., Global structural optimization of tungsten borides, Phys. Rev. Lett. 110 (13), 136403, 2013.
  2. Woods H. P., Jr. Wawner F. E., Fox G. B., Tungsten diboride: Preparation and structure, Science, 151 (3706), 75, 1966.
  3. Peshev P., Bliznakov G., Leyarovska L., On the preparation of some chromium, molybdenum and tungsten borides, J. Less Common Met., 13 (2), 241–247, 1967.
  4. Armas B., Trombe F., Chemical vapour deposition of molybdenum and tungsten borides by thermal decomposition of gaseous mixtures of halides on a solar “front chaud”, Solar Energy, 15 (1), 67–73, 1973.
  5. Tsirlin A. M., Khodov G. Ya., Zhigach A. F. Rabinovich R. A. Guzhov V. P., The electrical resistance of boron and of tungsten borides in boron filaments, J. Less Common Met., 67 (1), 137–141, 1979.
  6. Ellison E. G., Boone D. H., Some mechanical properties of boron-tungsten boride filaments, J. Less Common Met., 13 (1), 103–111, 1967.
  7. Itoh H., Matsudaira T., Naka S., Hamamoto H., Obayashi M., Formation process of tungsten borides by solid state reaction between tungsten and amorphous boron, J. Matter. Sci., 22 (8), 2811-2815, 1987.
  8. Radev D., Zahariev Z., Oxidation stability of B4C-MexBy, composite materials, J. Alloys Compd., 197 (1), 87–90, 1993.
  9. Otani S., Ishizawa Y., Preparation of WB2- x single crystals by the floating zone method, J. Cryst. Growth, 154 (1), 81-84, 1995.
  10. Okada S., Kudou K., Lundström T., Preparations and some properties of W2B, δ-WB and WB2 crystals from high-temperature metal solutions, Jpn. J. Appl. Phys., 34 (1), 226, 1995.
  11. Gostishchev V. V., Boiko V. F., Pinegina N. D., Magnesiothermal synthesis of W–WB powders in ionic melts”, Theor. Found. Chem. Eng, 43 (4), 468–472, 2009.
  12. Mohammadi R., Lech A. T., Xie M., Weaver B. E., Yeung M. T., Tolbert S. H., Kaner R. B., Tungsten tetraboride, an inexpensive superhard material, Proc. Nation. Acad. Sci., 108 (27), 10958–62, 2011.
  13. Yeh C. L., Wang H. J., Preparation of tungsten borides by combustion synthesis involving borothermic reduction of WO3, Ceram. Int., 37 (7), 2597–2601, 2011.
  14. Yazici S., Derin B., Effects of process parameters on tungsten boride production from WO3 by self-propagating high temperature synthesis, Matter. Sci. Eng. B, 178 (1), 89–93, 2013.
  15. Yazici S., Derin B., Production of tungsten boride from CaWO4 by self-propagating high-temperature synthesis followed by HCl leaching, Int. J. Refract. Met. Hard Mater., 29 (1), 90–95, 2011.
  16. Khor K. A., Yu L. G., Sundararajan G., Formation o