Farklı puzolanların tekli, ikili ve üçlü çimentolu sistemleri içeren harç karışımlarının dayanımı ve geçirgenlik performansı açısından kıyaslanması

Comparison of different pozzolans from strength and permeability performance of mortar mixtures containing plain, binary and ternary cementitious systems view point

Ali MARDANI-AGHABAGLOU
Süleyman ÖZEN
Sultan Husein BAYQRA
Hassane Amidou OUEDRAOGO
Sayfa
612–625
Yayın Tarihi
2018-05-14
DOI
—
🏛️Bu makalenin bibliyografik verileri ve tam metin bağlantısı DergiPark üzerinden sağlanmıştır.
DergiPark Kaydı ↗
✨

Yapay Zeka Hızlı Bakış & Çıkarımlar

AI Insight
⚡ TL;DR(1 Cümlede Hızlı Çıkarım)

Ancak 28 günden sonra hem metakaolin hem de silis dumanı içeren üçlü çimentolu sisteme sahip karışım en başarılı sonucu göstermiştir.

📌 3 Maddede Bu Makale

🎯
Amaç & Hipotez:Bu çalışmada silis dumanı ve metakaolin kullanımının tekli, ikili ve üçlü çimentolu sistemleri içeren harç karışımlarının dayanımına, geçirgenlik özelliğine ve ultra ses geçiş hızına etkisi kıyaslamalı olarak incelenmiştir.
📊
Temel Bulgular & Veri:Bu amaçla mineral katkı içermeyen kontrol karışımına ilaveten farklı oranlarda silis dumanı ve metakaolin çimento ile yer değiştirerek 3 seri karışım daha yapılmıştır. 1. ve 2. seride çimentonun %7,5’u ile ağırlıkça metakaolin ve silis dumanı yer değiştirmiştir. 3. seride ise çimentonun %7,5’u kadar hem metakaolin hem de silis dumanı kullanılarak toplamda %15 mineral katkı içeren karışım hazırlanmıştır.
💡
Sonuç & Katkı:Ancak 28 günden sonra hem metakaolin hem de silis dumanı içeren üçlü çimentolu sisteme sahip karışım en başarılı sonucu göstermiştir.
🔬Tür:Araştırma Makalesi
📍Kapsam:Genişletilmiş Akademik Örneklem
⚙️Değişkenler:Metakaolin · silica fume · mortar mixture

Özet

Bu çalışmada silis dumanı ve metakaolin kullanımının tekli, ikili ve üçlü çimentolu sistemleri içeren harç karışımlarının dayanımına, geçirgenlik özelliğine ve ultra ses geçiş hızına etkisi kıyaslamalı olarak incelenmiştir. Bu amaçla mineral katkı içermeyen kontrol karışımına ilaveten farklı oranlarda silis dumanı ve metakaolin çimento ile yer değiştirerek 3 seri karışım daha yapılmıştır. 1. ve 2. seride çimentonun %7,5’u ile ağırlıkça metakaolin ve silis dumanı yer değiştirmiştir. 3. seride ise çimentonun %7,5’u kadar hem metakaolin hem de silis dumanı kullanılarak toplamda %15 mineral katkı içeren karışım hazırlanmıştır. Tüm karışımlarda su/çimento oranı, kum/bağlayıcı oranı ve yayılma değeri sabit tutulmuştur. İstenilen yayılma değerini sağlamak için farklı oranlarda tek tip su azaltıcı katkı kullanılmıştır. Karışımların zamana bağlı yayılma değerleri, basınç ve eğilme dayanımları, su emme kapasiteleri ve ultra ses geçiş hızları belirlenmiştir. Deney sonuçlarına göre mineral katkı türünden bağımsız olarak mineral katkı kullanımı ile karışımların zamana bağlı yayılma, dayanım, geçirgenlik ve ultra ses geçiş hızı değerleri olumlu etkilenmiştir. Bu etki zamanla daha belirgin hale gelmiştir. İkili çimentolu sisteme sahip metakaolin içeren karışım erken yaşlarda diğer karışımlara göre daha iyi performans göstermiştir. Ancak 28 günden sonra hem metakaolin hem de silis dumanı içeren üçlü çimentolu sisteme sahip karışım en başarılı sonucu göstermiştir.

Abstract

In this study, the effect of silica fume and metakaolin on the strength, transport properties and ultrasonic pulse velocity of the mortar mixtures containing plain, binary and ternary cementitious systems were investigated comparatively. For this purpose, in addition to the control mixture containing no mineral admixture, three series of mixtures were produced by replacing silica fume and metakaolin with cement in different ratios. In the first and second series mixture, metakaolin and silica fume were used as 7.5wt% of the cement, respectively. In the third series, a mixture containing 15% of mineral admixture was prepared by replacing both silica fume and metakaolin with 7.5wt% of cement. In the all of mixture, the water/cement ratio, sand/binder ratio and flow values were kept constant. Water reducing admixture was used in different ratio for providing the desired flow values. The time-dependent flow value, compressive and flexural strengths, water absorption capacity and ultrasonic pulse velocity of the mixtures were determined. According to the test results, irrespective of utilization of mineral admixture, the time-dependent flow value, strength, permeability and ultrasonic pulse velocity of the mixtures were positively affected by using admixture. This effect was more pronounced by elapsing time. In the early ages, the metakaolin-bearing mixture with binary cementitious system showed better performance compare to the other mixtures. However, after 28 days, the mixture containing both metakaolin and silica fume with ternary cementitious system showed the most successful results.

🔖

Bu Makaleye Atıf Yap

MARDANI-AGHABAGLOU, A., ÖZEN, S., BAYQRA, S. H., OUEDRAOGO, H. A. (2018). Farklı puzolanların tekli, ikili ve üçlü çimentolu sistemleri içeren harç karışımlarının dayanımı ve geçirgenlik performansı açısından kıyaslanması. Balıkesir Üniversitesi Fen Bilimleri Enstitüsü Dergisi, Cilt: 20 - Sayı: 1, 612–625. https://ajindex.com/articles/251059

📄 Tam Metin PDF Okuyucu

📄

PDF görüntüleyici hazırlanıyor...

Kaynakça (16)

  1. Mehta, P.K., ve Monteiro, P.J.M., Concrete: microstructure, properties, and materials, (3th ed.), NJ: McGraw- Hill., (2006).
  2. Mindess, S., Young, J.F., ve Darwin, D., Concrete, second ed., Prentice-Hall, Upper Saddle River, NJ., (2003).
  3. Baradan, B., Türkel, S., Yazıcı, H., Ün H., Yiğiter, H., Felekoğlu, B., Tosun Felekoğlu, K., Aydın, S., Yardımcı, M. Y., Topal, A., Öztürk, A.U., Beton, Dokuz Eylül Üniversitesi Mühendislik Fakültesi Yayınları No: 334, İzmir, (2012).
  4. Erdoğan, T.Y., Beton. ODTÜ yayınları, Ankara, (2003).
  5. Malhotra, V.M., Ramachandran, V.S., Feldman, R.F., and Aitcin, P.C., Condensed silica fume in concrete, Boca Raton, FL: CRC Press, (1987).
  6. Swamy, R.N., Cement replacement materials, Vol. 3, London: Surrey University Press., (1986).
  7. Inan Sezer, G., Compressive strength and sulfate resistance of limestone and/or silica fume mortars, Construction and Building Materials, 26(1), 613–618, (2012).
  8. Giner, V.T., Ivorra, S., Baeza, F.J., Zornoza, E., ve Ferrer, B., Silica fume admixture effect on the dynamic properties of concrete, Construction and Building Materials, 25(8), 3272-3277, (2011).
  9. Mardani-Aghabaglou, A., Sezer, G. İ., ve Ramyar, K., Comparison of fly ash, silica fume and metakaolin from mechanical properties and durability performance of mortar mixtures view point, Construction and Building Materials, 70, 17-25, (2014).
  10. Wild, S., Khatib, J.M., ve Jones, A., Relative strength, pozzolanic activity and cement hydration in superplasticised metakaolin concrete, Cement and Concrete Research, 26, 10, 1537-1544, (1996).
  11. Shekarchi, M., Bonakdar, A., Bakhshi, M., Mirdamadi, A., ve Mobasher, B., Transport properties in metakaolin blended concrete, Construction and Building Materials, 24(11), 2217-2223, (2010).
  12. Poon, C.S., Kou, S.C., ve Lam, L., Compressive strength, chloride diffusivity and pore structure of high performance metakaolin and silica fume concrete, Construction and Building Materials, 20(10), 858-865, (2006).
  13. Curcio, F., DeAngelis, B.A., ve Pagliolico, S., Metakaolin as a pozzolanic microfiller for high-performance mortars, Cement and Concrete Research, 28(6), 803-809, (1998).
  14. Maekawa, K., Chaube, R., ve Kishi, T., Modeling of concrete performance: hydration, microstructure formation and mass transport, Taylor & Francis Group, London, (1999).
  15. Mehta, P.K., ve Aïtcin, P.C., Principles underlying production of high-performance concrete, Cement, Concrete and Aggregates, 12(2), 70-78, (1990).
  16. Kadri, E.H., Kenai, S., Ezziane, K., Siddique, R.,