Journals / Textile and Apparel / 2008 / Cilt: 18 Sayı: 1
INVESTIGATION OF THE CHANGES OCCURRED IN THE INNER STRUCTURE OF WET SPUN ACRYLIC FIBERS BY USING X-RAY DIFFRACTION METHOD ON THE FIBER PRODUCTION STAGES
- Journal
- Textile and Apparel
- Pages
- 15–22
- DOI
- —
Abstract
Acrylic fibers are the most useful fibers among the synthetic fibers in textile applications. The properties of synthetic fibers are affected by several production parameters. In this paper, the production of wet spun acrylic fibers from poly (acrylonitrile / vinyl acetate) copolymers was performed with a dimethyl acetamide (DMAc) / water coagulation bath. During wet spinning of acrylic fibers, fiber samples are taken from each fiber production stage. X-ray diffraction graphics of these fiber samples are obtained by wide angle xray diffraction instrument. During the production of polyacrylonitrile fibers by using wet spinning method, the changes occurred in the inner structure of fibers were researched by investigation of their x-ray diffraction graphics
Özet
Akrilik lifleri tekstil uygulamalarındaki en kullanışlı sentetik lifler arasında yer almaktadır. Sentetik liflerin özellikleri üretim esnasındaki birçok üretim parametresinden etkilenmektedir. Bu çalışmada Poli (akrilonitril / vinil asetat) kopolimerlerinden oluşan akrilik lifleri dimetil asetamid (DMAc) / su’dan oluşan koagülasyon banyosunda yaş çekim yöntemi kullanılarak üretilmiştir. Akrilik liflerinin yaş çekim yöntemi ile üretimi esnasında her üretim basamağından ayrı ayrı lif numuneleri alınmıştır. Geniş açı x-ışını difraksiyonu cihazı kullanılarak üretim basamaklarından alınan bu akrilik lif numunelerinin geniş açı x-ışını difraksiyon grafikleri elde edilmiştir. Elde edilen geniş açı x-ışını difraksiyonu grafikleri incelenerek yaş çekim yöntemi ile poliakrilonitril lif üretiminde işlem basamaklarında liflerin içyapılarında meydana gelen değişiklikler araştırılmaya çalışılmıştır