Effect Of Corrosion To RC Building Earthquake Damage

Abstract

Reinforced concrete and steel structures are designed by considering dead, live and seismic loads. But when earthquake damages are examined, it’s observed that; corrosion, which is not considered during design, increases the earthquake damage ratio of structural elements. Corrosion, which is a serious threat for structures in their service life, is a chemical and electrochemical reaction of metals and their environments. Corrosion causes the loss of metallic properties of metals. Most of the metals are not durable to water and atmospheric effects. For corrosion, there must be oxygen, humidity and electrolyte. In this paper; reasons and steps of corrosion and reinforcement steels, effects of corrosion to earthquake damage of structures and precautions for existing and planning structures are studied.

Özet

Günümüz betonarme ve çelik yapılar, kendi zati ağırlıkları, servis ve sismik yüklere göre boyutlandırılır. Ancak yapılardaki deprem hasarları incelendiğinde, boyutlandırmada belirgin bir şekilde dikkate alınmayan korozyonun yapıların deprem hareketinden hasar görmesini önemli ölçüde artırdığı gözlenmiştir. Betonarme yapıları içindeki donatıyı servis ömürleri boyunca tehdit eden korozyon, metalin içinde bulunduğu ortam ile kimyasal veya elektrokimyasal reaksiyona girerek metalik özelliklerini kaybetmesidir. Metallerin büyük bir kısmı su ve atmosfer etkisine dayanıklı olmayıp, normal şartlar altında bile korozyona uğrarlar. Korozyon oluşması için oksijen, nem ve elektrolit parametrelerin olması gerekir. Bu çalışmada, betonarme donatılarda korozyonun oluşum nedenleri ve aşaması incelenmektedir. Ayrıca korozyonun yapılardaki deprem hasarlarına etkisi ve oluşmaması için mevcut ve planlanan yapılarda alınması gereken önlemler irdelenmektedir.

Keywords: Korozyon, Sismik yük, Kimyasal reaksiyon, Betonarme donatı, Karbonasyon