A Study on Austempering a Hıgh Carbon Powder Metal Steel

Bir Yüksek Karbonlu Toz Metal Çeliğin Östemperlenmesi Üzerine Bir Çalışma

Abstract

In this study, 1.5% by weight of natural graphite powders were added to NC 100.24 pure iron powders to obtain plain high carbon steel powder metallurgy specimens. After respectively uniaxial pressing at room temperature, 100 °C and 200 °C and under 700 MPa pressing pressure, the specimens were sintered in an atmospheric controlled furnace at 1150 ° C. The spec,mens were then austenitized at 950 ° C for half an hour in a salt bath at 300 ° C for austempering heat treatment. The structure transformations after the heat treatment were examined using optic microscope. Through pressing processes at different temperatures, the effects of densification rate on the hardness and bainitic transformation were investigated. It was seen that by increasing the densitity of high carbon powder metal materials, the bainitic structure transformation was improved and thus hardness value was effectively increased.

Özet

Bu çalışmada NC100.24 saf demir tozlarına ağırlıkça %1,5 oranında doğal grafit tozları ilave edilerek sade yüksek karbonlu çelik toz metalurjisi numuneler elde edilmiştir. Hazırlanan karışım oda sıcaklığı, 100°C ve 200°C sıcaklıkta ve 700 Mpa presleme basıncında tek eksenli preslendikten sonra 1150°C de atmosfer kontrollü fırında sinterlenmiştir. Ardından östemperleme ısıl işlemi için numuneler 950°C de östenitlenip 300 °C sıcaklıktaki tuz banyosunda 30 dakika süre ile östemperleme işlemine tabi tutulmuştur. Isıl işlem sonrası gerçekleşen yapı dönüşümleri optik mikroskop yardımıyla incelenmiştir. Farklı sıcaklıklarda presleme işlemleriyle yoğunlaşma oranın sertlik ve beynitik dönüşünlere etkileri çalışılmıştır. Yüksek carbonlu toz metal malzemelerin yoğunluklarının artırılmasıyla, beynitik yapı dönüşümleri geliştirilmiş ve sertlik değerleri etkili bir şekilde artırılımıştır.