Al2O3- TiO2 (%97-3) SERAMİK TOZ PARÇACIK İLAVELİ CAM ELYAF TAKVİYELİ EPOKSİ MATRİSLİ KOMPOZİT MALZEMELERİN MEKANİKSEL ÖZELLİKLERİNİN İNCELENMESİ
- Pages
- 33–40
- DOI
- —
Abstract
In this study, an experimental study has been carried out to investigate the mechanical properties of glassfiber reinforced epoxy composite filled with different proportions of Al2O3- TiO2 (%97-3) particles. The weight fractions of the filler in the matrix were 5, 10, and 15 %. A commercially available plain-weave woven fabric with areal weight of the fabric is 270 g/m2 was used as reinforcement material. The tensile tests were conducted according to the ASTM D3039-76 standard. The results showed that while ultimate tensile strength and Young’s modulus of the composites decreased with increasing Al2O3- TiO2 (%97-3) particles content.
Özet
Bu çalışmada; cam elyaf takviyeli polimer matrisli kompozit malzemelerde Al2O3- TiO2(%97-3) seramik toz ilave parçacıkların malzemenin mekaniksel özelliklerine etkisi deneysel olarak incelenmiştir. Dokuma kumaş olarak; düz dokuma 270 gr/m2’lik kumaşlar kullanılmıştır. Matris malzemesi olarak epoksi reçine kullanılmıştır. Al2O3- TiO2 seramik tozlar reçinenin içerisine %5, %10, %15 katkı oranlarında ilave edilmiştir. Çekme deneyleri ASTM D3039-76 standardına göre yapılmıştır. Sonuçlar; cam elyaf takviyeli polimer matrisli kompozit malzemelerde, Al2O3- TiO2 (%97-3) seramik tozların kompozit malzemenin içinde artmasıyla, kompozit malzemelerin çekme dayanımları ve elastisite modüllerinin azaldığını göstermiştir.