Effect of zinc incorporation on the density of defect states in a-Se85Te15 glassy alloy
- Journal
- Turkish Journal of Physics
- Pages
- 261–270
- DOI
- —
Abstract
Present work incorporates the study of d.c. conductivity measurements at high electric fields in vacuum evaporated thin films of Se85-xTe15Znx (x = 0, 2, 4, 6 and 10) glassy alloys. Current-Voltage (I-V) characteristics have been measured at various fixed temperatures. In these samples, at low electric fields, ohmic behavior is observed. However, at high electric fields (E \sim 104 V/cm), non ohmic behavior is observed. An analysis of the experimental data confirms the presence of space charge limited conduction (SCLC) in the glassy materials studied in the present case. From the fitting of the data to the theory of SCLC, the density of defect states (DOS) near Fermi level is calculated. It is found that the DOS is increasing with increase in concentration of Zn in pure binary Se85Te15 glassy system. The results obtained have been explained on the basis of some structural changes with third element Zn as an impurity in the pure binary Se85Te15 glassy alloy and have been correlated with the electronegativity difference between the elements used in making the aforesaid glassy systems.
Özet
Present work incorporates the study of d.c. conductivity measurements at high electric fields in vacuum evaporated thin films of Se85-xTe15Znx (x = 0, 2, 4, 6 and 10) glassy alloys. Current-Voltage (I-V) characteristics have been measured at various fixed temperatures. In these samples, at low electric fields, ohmic behavior is observed. However, at high electric fields (E \sim 104 V/cm), non ohmic behavior is observed. An analysis of the experimental data confirms the presence of space charge limited conduction (SCLC) in the glassy materials studied in the present case. From the fitting of the data to the theory of SCLC, the density of defect states (DOS) near Fermi level is calculated. It is found that the DOS is increasing with increase in concentration of Zn in pure binary Se85Te15 glassy system. The results obtained have been explained on the basis of some structural changes with third element Zn as an impurity in the pure binary Se85Te15 glassy alloy and have been correlated with the electronegativity difference between the elements used in making the aforesaid glassy systems.