Synthesis of Novel Type Terpolymer Poly(Eugenol-co-methylmethacrylate-cohydroxyethylmethacrylate) Using Photopolymerization Method: Characterization and Investigation of Thermal Properties
- Pages
- 1334–1347
- DOI
- —
Abstract
In this study, it has been demonstrated that Poly(Eugenol-co-methylmethacrylate-cohydroxyethylmethacrylate) terpolymers were successfully synthesized by using photopolymerization method. This synthesis was carried out in one step at ambient temperature, benzophenone and triethyl amine was used as the photoinitiator and hydrogen donor, respectively. Methyl methacrylate (MMA), 2-Hydroxyethyl methacrylate (HEMA) and Eugenol (Eg) were used as monomer in photopolymerization. Terpolymers are named as F-BAP1, F-BAP2, F-BAP3 and F-BAP4 according to the ratio of monomers used. Structural characterization and thermal properties of the synthesized terpolymers were carried out by FTIR (Fouriertransform infrared spectroscopy), 1H-NMR (Nuclear magnetic resonance spectroscopy), TG-DTG (Thermogravimetry-Differential Thermogravimetry) and DSC (Differential scanning calorimetry) methods. Characterization of molecular weight distributions were determined by viscometric method. SEM (Scanning electron microscope) was used for surface analysis. According to the data obtained from thermal analysis, two degradation steps are seen in thermograms of the terpolymers except FBAP-2. The maximum degradation temperature of F-BAP 2 is 422 oC, the first and second decomposition temperatures of F-BAP1, F-BAP2, FBAP3 are between 250-280 ° C and 421-427 ° C, respectively.
Özet
Bu çalışmada, Poly (Eugenol-ko-metilmetakrilat-ko-hidroksietilmetakrilat) terpolimerlerinin fotopolimerizasyon yöntemi kullanılarak başarıyla sentezlendiği gösterilmiştir. Bu sentez, ortam sıcaklığında bir aşamada gerçekleştirildi, sırasıyla foto başlatıcı ve hidrojen donör olarak benzofenon ve trietil amin kullanıldı. Fotopolimerizasyonda monomer olarak metil metakrilat (MMA), 2-Hidroksietil metakrilat (HEMA) ve Öjenol (Eg) kullanıldı. Terpolimerler kullanılan monomerlerin oranına göre F-BAP1, F-BAP2, F-BAP3 ve F-BAP4 olarak adlandırıldı. Sentezlenen terpolimerlerin yapısal karakterizasyonu ve termal özellikleri FTIR (Fourier-transform infrared spektroskopi), 1H-NMR (Nükleer manyetik rezonans spektroskopisi), TG-DTG (Termogravimetri-Diferansiyel Termogravimetri) ve DSC (Diferansiyel taramalı kalorimetri) yöntemleri ile gerçekleştirildi. Moleküler ağırlık dağılımları viskometrik yöntemle belirlendi. Yüzey analizi için SEM (Taramalı elektron mikroskobu) kullanıldı. Termal analizden elde edilen verilere göre terpolimerlerin termogramlarda FBAP-2 haricinde iki bozunma basamağı görülmektedir. F-BAP 2'nin maksimum bozunma sıcaklığı 422 oC, diğer terpolimerlerin birinci bozunma sıcaklığı 250-280 oC ve ikincisi 421-427 oC arasındadır.