The Effect of Bleaching Conditions on the Physical and Optical Properties During the Bleaching of CTMP with Peroxide

Kimyasal Termomekanik Kağıt Hamuru (CTMP)'nun Peroksit (P) ile Ağartılmasında Değişkenlerin Hamurun Fiziksel ve Optik Özelliklerine Etkisi

Abstract

In order to determine the effect of bleaching conditions on the physical and optical properties of pulps during the bleaching of CTMP with H2O2, 48 bleaching trials were carried out. After the analysis of the data obtained, the optimum bleaching conditions were as follows: H2O2 ratio 2.5-3%, Na2SiO3 ratio 3%, NaOH ratio 3%, NaOH/H2O2 ratio 0.75, MgSO4 rate 0.5%, reaction temperature 70ºC, EDTA rate 0.5%, reaction time 80 minutes and concentration 16%. Brightness, breaking length, burst and tear index of CTMP bleached with H2O2 were found to be 51.42%, 18.03%, 92.50% and 13.20% respectively, higher than those of unbleached CTMP

Özet

Bu çalışmada, kimyasal termomekanik kağıthamurunun (CTMP) H2O2 ile ağartılmasında; ağartma değişkenlerinin fiziksel ve optik özellikler üzerine olan etkisi belirlenmeye çalışılmıştır.Bu amaçla, 48 adet ağartma denemesi gerçekleştirilmiş olup elde edilen verilere dayanılarak optimum ağartma koşulları H2O2 oranı %2.5-3, Na2Si03 oranı %3, NaOH oranı %3, NaOH/H2O2 oranı 0.75, MgSO4 oranı %0.5, reaksiyon sıcaklığı 70ºC, EDTA oranı %0.5, reaksiyon süresi 80 dak., konsantrasyon %16 olarak belirlenmiştir. Böylece; ağartılmamış CTMP na göre H2O2 ile ağartılmış CTMP nın parlaklığı %51.42, kopma uzunluğu %18.03, yırtılma indisi %13.20 ve patlama indisi %92.50 oranında artmıştır.