PLASMA INDUCED GRAFT POLYMERIZATION OF A FLUOROCARBON MONOMER ON POLYAMIDE 6,6 FABRICS

POLIAMID 6,6 KUMAŞLARDA BİR FLOROKARBON MONOMERİNİN PLAZMA YARDIMI İLE AŞI POLİMERİZASYONU

Abstract

2-(perfluorohexyl) ethyl acrylate, a fluorocarbon based monomer was graft polymerized on polyamide 6,6 fabrics with the aid of an atmospheric pressure plasma reactor to obtain a water repellent surface. Di(ethylene glycol) diacrylate crosslinker was used to improve the graft yield of the polymerized layer. Two sets of experiments were conducted to understand the effects of variables on aqueous liquid repellency of fabrics. Plasma post exposure time and the presence of a crosslinker at high levels led to higher aqueous liquid repellency values and lower surface tension values. Static water contact angles were measured for the fabrics and values as high as 158 degrees were observed. FT-IR spectra also confirmed the high fluorocarbon content on the fabric surface after acetone extraction and after home laundering.

Özet

Florokarbon özellikli bir monomer olan 2-(perflorohegzil) etil akrilat, poliamid 6,6 kumaşlara uygulanmış ve atmosferik basınç plazma cihazı yardımıyla aşı polimerizasyonu gerçekleştirilmiştir. Plazma işlemi sonucunda su itici bir yüzey elde edilmiştir. Di(etilen glikol) diakrilat çapraz bağlayıcısı, polimerizasyon verimini artırmak için kullanılmıştır. Farklı değişkenlerin kumaşlardaki sıvı iticilik değerine etkisini incelemek için iki deney grubu oluşturulmuştur. Uzun plazma işlem süresi ve yüksek oranda çapraz bağlayıcı varlığında en iyi sıvı iticilik değerleri ve düşük yüzey gerilim değerleri gözlenmiştir. Kumaşların su ile statik temas açısı ölçümleri sonucu 158 derece kadar yüksek değerler gözlenmiştir. FT-IR analizi sonucunda, kumaşlarda asetonla ekstrakte sonrası ve yıkama sonrasında florokarbon içeren bir kimyasalın yüzeyde yüksek oranda bulunduğu kanıtlanmıştır.