EFFECT OF CALSIUM ALUMINATE CEMENT ON LIGHTWEIGHT PUMICE AGGREGATE CONCRETE PROPERTIES
- Pages
- 154–160
- DOI
- —
Abstract
The production of special concrete has accelerated together with the advancement of technology. In this study, it is aimed to compare the physical and mechanical properties of concrete which were made 500 doses of CEM I 42,5R and Calcium Aluminate Cement (CAC) and prepared by replacing the pumice in different proportions (25% and 100%) to the coarse aggregate (screen diameter 4/8 - 8/16 mm) of 100%. Unit weight and spread test on fresh concrete specimens produced for this purpose; dry unit weight, compressive strength, bending strength and tensile strength were tested on hardened concrete specimens. As a result of this study, in all concrete samples the highest compressive strength was obtained from concrete samples of CEM I 42.5 R (100-CSCEM) with 100% crushed stone aggregate.
Özet
B Teknolojinin ilerlemesiyle beraber özel betonların üretimi hız kazanmıştır. Bu çalışmada, %100 kırmataş agregalı betonun iri agregasına (elek çapı 4/8 - 8/16 mm) farklı oranlarda (%25 ve %100) pomza agregası ikame edilerek üretilen CEM I 42,5R ve Kalsiyum Alüminat Çimentolu (CAC) betonların fiziksel ve mekanik özelliklerinin karşılaştırılması amaçlanmıştır. Bu amaçla üretilen taze beton numuneleri üzerinde birim ağırlık ve yayılma deneyi; sertleşmiş beton numuneleri üzerinde kuru birim ağırlık, basınç dayanımı, yarmada çekme ve eğilme dayanımı deneyleri yapılmıştır. Çalışmanın sonucunda, tüm beton numuneleri içerisinde en yüksek basınç dayanımı %100 kırmataş agregalı CEM I 42,5 R (100-CSCEM) beton numunelerinden elde edilmiştir.