DAMAGE ANALYSIS OF COMPOSITE MATERIALS BY ULTRASONIC C SCAN METHOD AFTER CHARPY IMPACT TEST
- Pages
- 332–340
- DOI
- —
Abstract
In this study, the image of internal damage caused by the energy absorbed after impact in fiber reinforcedcomposites was investigated. In composite structures made of 14 layers of carbon and 14 layers of glass fabric, thematrix material variable was kept constant and the samples were produced in the same dimensions by vacuuminfusion method. These produced samples were subjected to impact with Charpy impact tester. The samples wereexamined according to through transmission ultrasonic test (TTU) method before and after the impact. Theresulting internal damage area was calculated using image processing methods from the C-Scan images. As aresult; It has been understood that there is a direct proportionality between the energy absorption rate from theCharpy test device and the damage spread and the area covered by the damaged area.
Özet
Bu çalışmada, elyaf takviyeli kompozitlerde darbe sonrası absorblanan enerji ile oluşan iç hasar görüntüsüaraştırılmıştır. 14 kat karbon ve 14 kat cam dokuma kumaştan oluşturulan kompozit yapılarda matris malzemedeğişkeni sabit tutularak vakum infüzyon yöntemi ile numuneler aynı boyutlarda üretilmiştir. Üretilen bunumuneler Charpy darbe test cihazı ile darbeye maruz bırakılmıştır. Numunelere darbe öncesinde ve sonrasındadoğrudan geçişli ultrasonik test (TTU) yöntemine göre muayene yapılmıştır. Elde edilen C-Tarama görüntülerindegörüntü işleme yöntemi kullanılarak, oluşan iç hasar alanı hesaplanmıştır. Sonuç olarak; Charpy test cihazındanalınan enerji absorblama oranı ile hasar yayılımı ve hasarlı bölgenin kapladığı alan arasında doğru orantı tespitedilmiştir.