Microleakage study of porcelain fused to metal alloys

Farklı metal alaşımlardan hazırlanan metal destekli porselenlerde mikrosızıntı

Abstract

The present article reports a study ofmicroleakage in the in¬terface between various metal alloys and porcelain. In this study chrome-nickel, chrome-cobalt and titanium alloys we¬re investigated. Microleakage specimen were prepared in the shape of 2.2 mm thick disks which were 1 cm in diame¬ter. Our findings showed similar microleakage in specimen sto¬red in water and those not stored in water. The results indicated that microleakage at porcelain fused to chrome-cobalt alloy was greater than that found for the ot¬her two alloys. No significant differences were found between the microlea¬kage at the interface of porcelain fused to titanium and por¬celain fused to chrome-nickel alloy.

Özet

Çalışmada metal destekli porselen ara yüzeyinde mik-rosızınn incelenmiştir. Bunun için krom-kobalt, krom-nikel ve titanyum alaşımlarından 1 cm çapında, lmm metal kalınlığı ve 1.2 mm porselen kalınlığı olan 20'şer adet örnek hazırlanmıştır. Sızıntı belirlemesinde oto-radyografi yöntemi kullanılmıştır. Her alaşım grubun¬daki örnekler suda beklemiş ve beklememiş olmak üzere ikiye ayrılmıştır. Çalışmanın sonucunda suda beklemiş ve beklememiş örneklerin sızıntıları arasında önemsiz fark olduğu bu¬lunmuştur. En fazla sızıntı krom-kobalt destekli porselen örnek¬lerde gözlenmiştir. Krom-nikel ve titanyum destekli porselen örnekler arasında ise mikrosızmtı farkı önemsiz bulunmuştur.